Method and catalyst system for preparing polymers and block copolymers

ABSTRACT

The present invention provides methods for producing block copolymers, either by the sequential addition of monomers, or using a “one-pot” method. The invention also relates to novel methods for producing polyesters by ring opening lactides and/or lactones and by copolymerising anhydrides and epoxides.

This application is a divisional of and claims priority under 35 U.S.C. § 120 to U.S. Application, U.S. Ser. No. 14/891,148, filed Nov. 13, 2015; which is a national stage filing under 35 U.S.C. § 371 of international PCT application, PCT/GB2014/051511, filed May 16, 2014, which claims priority under 35 U.S.C. § 119(a) to United Kingdom application number 1308978.4, filed May 17, 2013, each of which is incorporated herein by reference.

FIELD OF THE INVENTION

The present invention relates to methods for producing block copolymers, either by the sequential addition of monomers, or using a “one-pot” method. In particular, the chemistry of the catalyst active site allows selective polymerisation of particular monomers and control of block sequence in the production of block copolymers comprising polycarbonate blocks and polyester blocks, using a single catalytic system. It is possible to switch between the formation of a polyester and a polycarbonate by controlling the growing polymer chain end and by selecting the identity and amount of the monomers used. The methods described allow the product of the preparation of di-block copolymers, as well as more complex block sequences, including ABA and ABC type block copolymers. The invention also relates to novel methods for producing polyesters by ring opening lactides and/or lactones and by copolymerising anhydrides and epoxides.

BACKGROUND

Block copolymers are polymers having two or more distinct polymeric units, or “blocks”. Such polymers are useful in a variety of different applications, and it is particularly preferred to be able to produce block copolymers having polyester and polycarbonate blocks.

Block copolymers can be produced in a variety of different ways. For example, the individual blocks may be prepared separately, and then joined together. Alternatively, a first block, comprising an initiating moiety (also known as a “macroinitiator”) can be added to a mixture of one or monomers, and the second block is grown from the end of the pre-formed block. However, such methods require the formation and purification of the first blocks prior to the formation of a second block, and generally involve the use of different catalytic systems to produce each block. These methods can therefore be costly and difficult to use.

The inventors have surprisingly found that it is possible to produce block copolymers comprising two or more blocks, using a single catalytic system, either by the subsequent addition of monomer, or by a “one-pot” method in which all of the monomers are present in the reaction mixture at the start of the reaction.

SUMMARY OF THE INVENTION

In a first aspect, the present invention provides a method for preparing a block copolymer, using a single catalytic system, wherein the single catalytic system comprises a catalyst of formula (I):

Wherein:

[M] is a metal complex having at least one metal atom M coordinated by a ligand system;

M is Zn, Cr, Co, Mn, Mg, Fe, Ti, Ca, Ge, Al, Mo, W, Ru, Ni or V;

Z is absent, or is independently selected from -E-, -EX(E)-, or -EX(E)E-, each E is independently selected from O, S or NR^(Z), wherein R^(Z) is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl;

X is C or S

R is hydrogen, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl, alkylheteroaryl, silyl or a polymer; and when Z is absent, R may additionally be selected from halide, phosphinate, azide and nitrate;

the method comprising the steps of:

-   -   a) forming a first block by polymerising a first monomer or         combination of monomers selected from the groups (i) to (iii):         -   Group (i): a lactide and/or a lactone,         -   Group (ii): an epoxide and an anhydride, or         -   Group (iii): an epoxide and carbon dioxide,     -   b) optionally contacting the catalyst of formula (I) with a         compound [Y] which is capable converting the group —Z—R, wherein         Z is absent or a group selected from -E-X(E)- or -E-X(E)E-, to a         group —Z—R wherein Z is -E-;     -   c) forming a second block by polymerising a second monomer or         combination of monomers selected from a different group (i)         to (iii) to that selected for the first monomer or combination         of monomers:         -   Group (i): a lactide and/or a lactone,         -   Group (ii): an epoxide and an anhydride, or         -   Group (iii): an epoxide and carbon dioxide,

wherein when the first monomer or combination of monomers is Group (i), Z is -E-; and

wherein when the first monomer or combination of monomers is Group (ii) or Group (iii),

and the second monomer or combination of monomers is Group (i), step b) is performed after step a).

In a second aspect, the present invention provides a method for producing a block copolymer, said block copolymer having a first and second block, using a single catalytic system, wherein the single catalytic system comprises a catalyst of formula (I):

Wherein:

[M] is a metal complex having at least one metal atom M coordinated by a ligand system;

M is Zn, Cr, Co, Mn, Mg, Fe, Ti, Ca, Ge, Al, Mo, W, Ru, Ni or V;

Z is absent, or is independently selected from -E-, -EX(E)-, or -EX(E)E-,

each E is independently selected from O, S or NR^(Z), wherein R^(Z) is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl;

X is C or S

R is hydrogen, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl, alkylheteroaryl, silyl or a polymer; and when Z is absent, R may also be selected from halide, phosphinate, azide and nitrate;

the method comprising the steps of:

-   -   a) providing a mixture comprising:         -   I. an epoxide;         -   II. a first monomer or combination of monomers selected from             a group (i) to (iii):             -   Monomer (i): a lactide and/or a lactone,             -   Monomer (ii): an anhydride, or             -   Monomer (iii): carbon dioxide, and         -   III. a second monomer or combination of monomers selected             from a different group (i) to (iii) to that selected for the             first monomer or combination of monomers:             -   Monomer (i): a lactide and/or a lactone,             -   Monomer (ii): an anhydride, or             -   Monomer (iii): carbon dioxide; and     -   b) contacting the mixture with the single catalytic system;

wherein the rate of insertion of the first monomer or combination of monomers into the bond between the metal complex [M] and the ligand —Z—R is faster than the rate of insertion of the second monomer or combination of monomers into the bond between the metal complex [M] and the ligand —Z—R;

wherein when the first monomer or combination of monomers is Group (i), either —Z—R is -E-R, or the mixture comprises a compound [Y]; and

wherein when the second monomer or combination of monomers is Group (i), the mixture comprises a compound [Y].

In a third aspect, the present invention provides a method for producing a polyester, comprising contacting a lactone and/or a lactide with a catalyst system having a catalyst of formula (IA):

wherein

R₁ and R₂ are independently hydrogen, halide, a nitro group, a nitrile group, an imine, an amine, an ether group, a silyl ether group, a thioether group, a sulfoxide group, a sulfinate group, or an acetylide group or an optionally substituted alkyl, alkenyl, alkynyl, haloalkyl, aryl, heteroaryl, alicyclic or heteroalicyclic;

R₃ is optionally substituted alkylene, alkenylene, alkynylene, heteroalkylene, heteroalkenylene, heteroalkynylene, arylene, heteroarylene or cycloalkylene, wherein alkylene, alkenylene, alkynylene, heteroalkylene, heteroalkenylene and heteroalkynylene may optionally be interrupted by aryl, heteroaryl, alicyclic or heteroalicyclic;

R₄ is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylheteroaryl or alkylaryl;

R₅ is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylheteroaryl or alkylaryl;

E₁ is C, E₂ is O, S or NH or E₁ is N and E₂ is O;

R is hydrogen, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl, alkylheteroaryl silyl, or a polymer;

Z is -E-;

E is —O—, —S—, or NR^(Z), wherein is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl;

each G is independently absent or a neutral or anionic donor ligand which is a Lewis base; and

M is Zn(II), Cr(II), Co(II), Mn(II), Mg(II), Fe(II), Ti(II), Cr(III)-Z—R, Co(III)Z—R, Mn (III)-Z—R, Fe(III)-Z—R, Ca(II), Ge(II), Al(III)-Z—R, Ti(III)-Z—R, V(III)-Z—R, Ge(IV)-(—Z—R)₂ or Ti(IV)-(—Z—R)₂.

In a fourth aspect of the invention, there is provided method for producing a polyester, comprising contacting an anhydride and an epoxide with a catalyst system having a catalyst of formula (IA):

wherein

R₁ and R₂ are independently hydrogen, halide, a nitro group, a nitrile group, an imine, an amine, an ether group, a silyl ether group, a thioether group, a sulfoxide group, a sulfinate group, or an acetylide group or an optionally substituted alkyl, alkenyl, alkynyl, haloalkyl, aryl, heteroaryl, alicyclic or heteroalicyclic;

R₃ is optionally substituted alkylene, alkenylene, alkynylene, heteroalkylene, heteroalkenylene, heteroalkynylene, arylene, heteroarylene or cycloalkylene, wherein alkylene, alkenylene, alkynylene, heteroalkylene, heteroalkenylene and heteroalkynylene may optionally be interrupted by aryl, heteroaryl, alicyclic or heteroalicyclic;

R₄ is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylheteroaryl or alkylaryl;

R₅ is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylheteroaryl or alkylaryl;

E₁ is C, E₂ is O, S or NH or E₁ is N and E₂ is O;

Z is absent, or is selected from -E-, -EX(E)-, or -EX(E)E-;

X is S or C;

E is —O—, —S—, or NR^(Z), wherein is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl;

R is hydrogen, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl, alkylheteroaryl, or silyl, or a polymer; and when Z is absent, R may additional be selected from halide, phosphinate, azide and nitrate;

each G is independently absent or a neutral or anionic donor ligand which is a Lewis base; and

M is Zn(II), Cr(II), Co(II), Mn(II), Mg(II), Fe(II), Ti(II), Cr(III)-Z—R, Co(III)-Z—R, Mn (III)-Z—R, Fe(III)-Z—R, Ca(II), Ge(II), Al(III)-Z—R, Ti(III)-Z—R, V(III)-Z—R, Ge(IV)-(—Z—R)₂ or Ti(IV)-(—Z—R)₂.

In a fifth aspect of the invention, there is provided a polymer obtainable from the method according to any of the first, second, third or fourth aspects of the invention.

Definitions

For the purpose of the present invention, an aliphatic group is a hydrocarbon moiety that may be straight chain or branched and may be completely saturated, or contain one or more units of unsaturation, but which is not aromatic. The term “unsaturated” means a moiety that has one or more double and/or triple bonds. The term “aliphatic” is therefore intended to encompass alkyl, alkenyl or alkynyl groups, and combinations thereof. An aliphatic group is preferably a C₁₋₂₀aliphatic group, that is an aliphatic group with 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19 or 20 carbon atoms. Preferably, an aliphatic group is a C₁₋₁₅aliphatic, more preferably a C₁₋₁₂aliphatic, more preferably a C₁₋₁₀aliphatic, even more preferably a C₁₋₈aliphatic, such as a C₁₋₆aliphatic group.

An alkyl group is preferably a “C₁₋₂₀ alkyl group”, that is an alkyl group that is a straight or branched chain with 1 to 20 carbons. The alkyl group therefore has 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19 or 20 carbon atoms. Preferably, an alkyl group is a C₁₋₁₅alkyl, preferably a C₁₋₁₂alkyl, more preferably a C₁₋₁₀alkyl, even more preferably a C₁₋₈alkyl, even more preferably a C₁₋₆alkyl group. In certain embodiments, an alkyl group is a “C₁₋₆ alkyl group”, that is an alkyl group that is a straight or branched chain with 1 to 6 carbons. The alkyl group therefore has 1, 2, 3, 4, 5 or 6 carbon atoms. Specifically, examples of “C₁₋₂₀ alkyl group” include methyl group, ethyl group, n-propyl group, iso-propyl group, n-butyl group, iso-butyl group, sec-butyl group, tert-butyl group, n-pentyl group, n-hexyl group, n-heptyl group, n-octyl group, n-nonyl group, n-decyl group, n-undecyl group, n-dodecyl group, n-tridecyl group, n-tetradecyl group, n-pentadecyl group, n-hexadecyl group, n-heptadecyl group, n-octadecyl group, n-nonadecyl group, n-eicosyl group, 1,1-dimethylpropyl group, 1,2-dimethylpropyl group, 2,2-dimethylpropyl group, 1-ethylpropyl group, n-hexyl group, 1-ethyl-2-methylpropyl group, 1,1,2-trimethylpropyl group, 1-ethylbutyl group, 1-methylbutyl group, 2-methylbutyl group, 1,1-dimethylbutyl group, 1,2-dimethylbutyl group, 2,2-dimethylbutyl group, 1,3-dimethylbutyl group, 2,3-dimethylbutyl group, 2-ethylbutyl group, 2-methylpentyl group, 3-methylpentyl group and the like. Alkenyl and alkynyl groups are preferably “C₂₋₂₀alkenyl” and “C₂₋₂₀alkynyl” respectively, that is an alkenyl or alkynyl group which is a straight chain or branched chain with 2 to 20 carbons. The alkenyl or alkynyl group therefore has 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19 or 20 carbon atoms. Preferably, an alkenyl group or an alkynyl group is “C₂₋₁₅alkenyl” and “C₂₋₁₅alkynyl”, more preferably “C₂₋₁₂alkenyl” and “C₂₋₁₂alkynyl”, even more preferably “C₂₋₁₀alkenyl” and “C₂₋₁₀alkynyl”, even more preferably “C₂₋₈alkenyl” and “C₂₋₈alkynyl”, most preferably “C₂₋₆alkenyl” and “C₂₋₆alkynyl” groups respectively.

A heteroaliphatic group is an aliphatic group as described above, which additionally contains one or more heteroatoms. Heteroaliphatic groups therefore preferably contain from 2 to 21 atoms, preferably from 2 to 16 atoms, more preferably from 2 to 13 atoms, more preferably from 2 to 11 atoms, more preferably from 2 to 9 atoms, even more preferably from 2 to 7 atoms, wherein at least one atom is a carbon atom. Particularly preferred heteroatoms are selected from O, S, N, P and Si. When heteroaliphatic groups have two or more heteroatoms, the heteroatoms may be the same or different.

An alicyclic group is a saturated or partially unsaturated cyclic aliphatic monocyclic or polycyclic (including fused, bridging and spiro-fused) ring system which has from 3 to 20 carbon atoms, that is an alicyclic group with 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19 or 20 carbon atoms. Preferably, an alicyclic group has from 3 to 15, more preferably from 3 to 12, even more preferably from 3 to 10, even more preferably from 3 to 8 carbon atoms. The term “alicyclic” encompasses cycloalkyl, cycloalkenyl and cycloalkynyl groups. It will be appreciated that the alicyclic group may comprise an alicyclic ring bearing one or more linking or non-linking alkyl substitutents, such as —CH₂-cyclohexyl.

Cycloalkyl, cycloalkenyl and cycloalkynyl groups have from 3 to 20 carbon atoms. The cycloalkyl, cycloalkenyl and cycloalkynyl groups therefore have 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19 or 20 carbon atoms. Cycloalkyl, cycloalkenyl and cycloalkynyl groups preferably have from 3 to 15, more preferably from 3 to 12, even more preferably from 3 to 10, even more preferably from 3 to 8 carbon atoms. When an alicyclic group has from 3 to 8 carbon atoms, this means that the alicyclic group has 3, 4, 5, 6, 7 or 8 carbon atoms. Specifically, examples of the C₃₋₂₀ cycloalkyl group include cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, adamantyl and cyclooctyl.

A heteroalicyclic group is an alicyclic group as defined above which has, in addition to carbon atoms, one or more ring heteroatoms, which are preferably selected from O, S, N, P and Si. Heteroalicyclic groups preferably contain from one to four heteroatoms, which may be the same or different. Heterocyclic groups preferably contain from 4 to 20 atoms, more preferably from 4 to 14 atoms, even more preferably from 4 to 12 atoms.

An aryl group is a monocyclic or polycyclic ring system having from 5 to 20 carbon atoms. An aryl group is preferably a “C₆₋₁₂ aryl group” and is an aryl group constituted by 6, 7, 8, 9, 10, 11 or 12 carbon atoms and includes condensed ring groups such as monocyclic ring group, or bicyclic ring group and the like. Specifically, examples of “C₆₋₁₀ aryl group” include phenyl group, biphenyl group, indenyl group, naphthyl group or azulenyl group and the like. It should be noted that condensed rings such as indan and tetrahydro naphthalene are also included in the aryl group.

A heteroaryl group is an aryl group having, in addition to carbon atoms, from one to four ring heteroatoms which are preferably selected from O, S, N, P and Si. A heteroaryl group preferably has from 5 to 20, more preferably from 5 to 14 ring atoms. Specifically, examples of a heteroaryl group includes pyridine, imidazole, N-methylimidazole and 4-dimethylaminopyridine.

Examples of alicyclic, heteroalicyclic, aryl and heteroaryl groups include but are not limited to cyclohexyl, phenyl, acridine, benzimidazole, benzofuran, benzothiophene, benzoxazole, benzothiazole, carbazole, cinnoline, dioxin, dioxane, dioxolane, dithiane, dithiazine, dithiazole, dithiolane, furan, imidazole, imidazoline, imidazolidine, indole, indoline, indolizine, indazole, isoindole, isoquinoline, isoxazole, isothiazole, morpholine, napthyridine, oxazole, oxadiazole, oxathiazole, oxathiazolidine, oxazine, oxadiazine, phenazine, phenothiazine, phenoxazine, phthalazine, piperazine, piperidine, pteridine, purine, pyran, pyrazine, pyrazole, pyrazoline, pyrazolidine, pyridazine, pyridine, pyrimidine, pyrrole, pyrrolidine, pyrroline, quinoline, quinoxaline, quinazoline, quinolizine, tetrahydrofuran, tetrazine, tetrazole, thiophene, thiadiazine, thiadiazole, thiatriazole, thiazine, thiazole, thiomorpholine, thianaphthalene, thiopyran, triazine, triazole, and trithiane.

The term “halide” or “halogen” are used interchangeably and, as used herein mean a fluorine atom, a chlorine atom, a bromine atom, an iodine atom and the like, preferably a fluorine atom, a bromine atom or a chlorine atom, and more preferably a fluorine atom or a bromine atom.

A haloalkyl group is preferably a “C₁₋₂₀ haloalkyl group”, more preferably a “C₁₋₁₅ haloalkyl group”, more preferably a “C₁₋₁₂ haloalkyl group”, more preferably a “C₁₋₁₀ haloalkyl group”, even more preferably a “C₁₋₈ haloalkyl group”, even more preferably a “C₁₋₆ haloalkyl group” and is a C₁₋₂₀ alkyl, a C₁₋₁₅ alkyl, a C₁₋₁₂ alkyl, a C₁₋₁₀ alkyl, a C₁₋₈ alkyl, or a C₁₋₆ alkyl group, respectively, as described above substituted with at least one halogen atom, preferably 1, 2 or 3 halogen atom(s). Specifically, examples of “C₁₋₂₀ haloalkyl group” include fluoromethyl group, difluoromethyl group, trifluoromethyl group, fluoroethyl group, difluroethyl group, trifluoroethyl group, chloromethyl group, bromomethyl group, iodomethyl group and the like.

An alkoxy group is preferably a “C₁₋₂₀ alkoxy group”, more preferably a “C₁₋₁₅ alkoxy group”, more preferably a “C₁₋₁₂ alkoxy group”, more preferably a “C₁₋₁₀ alkoxy group”, even more preferably a “C₁₋₈ alkoxy group”, even more preferably a “C₁₋₆ alkoxy group” and is an oxy group that is bonded to the previously defined C₁₋₂₀ alkyl, C₁₋₁₅ alkyl, C₁₋₁₂ alkyl, C₁₋₁₀ alkyl, C₁₋₈ alkyl, or C₁₋₆ alkyl group respectively. Specifically, examples of “C₁₋₂₀alkoxy group” include methoxy group, ethoxy group, n-propoxy group, iso-propoxy group, n-butoxy group, iso-butoxy group, sec-butoxy group, tert-butoxy group, n-pentyloxy group, iso-pentyloxy group, sec-pentyloxy group, n-hexyloxy group, iso-hexyloxy group, n-hexyloxy group, n-heptyloxy group, n-octyloxy group, n-nonyloxy group, n-decyloxy group, n-undecyloxy group, n-dodecyloxy group, n-tridecyloxy group, n-tetradecyloxy group, n-pentadecyloxy group, n-hexadecyloxy group, n-heptadecyloxy group, n-octadecyloxy group, n-nonadecyloxy group, n-eicosyloxy group, 1,1-dimethylpropoxy group, 1,2-dimethylpropoxy group, 2,2-dimethylpropoxy group, 2-methylbutoxy group, 1-ethyl-2-methylpropoxy group, 1,1,2-trimethylpropoxy group, 1,1-dimethylbutoxy group, 1,2-dimethylbutoxy group, 2,2-dimethylbutoxy group, 2,3-dimethylbutoxy group, 1,3-dimethylbutoxy group, 2-ethylbutoxy group, 2-methylpentyloxy group, 3-methylpentyloxy group and the like.

An alkylthio group is preferably a “C₁₋₂₀ alkylthio group”, more preferably a “C₁₋₁₅ alkylthio group”, more preferably a “C₁₋₁₂ alkylthio group”, more preferably a “C₁₋₁₀ alkylthio group”, even more preferably a “C₁₋₈ alkylthio group”, even more preferably a “C₁₋₆ alkylthio group” and is a thio (—S—) group that is bonded to the previously defined C₁₋₂₀ alkyl, C₁₋₁₅ alkyl, C₁₋₁₂ alkyl, C₁₋₁₀ alkyl, C₁₋₅ alkyl, or C₁₋₆ alkyl group respectively.

An alkylaryl group can comprise any of the alkyl or aryl groups discussed above. Preferably the alkylaryl group is a “C₆₋₁₂ aryl C₁₋₂₀ alkyl group”, more preferably a preferably a “C₆₋₁₂ aryl C₁₋₁₆ alkyl group”, even more preferably a “C₆₋₁₂ aryl C₁₋₆ alkyl group” and is an aryl group as defined above bonded at any position to an alkyl group as defined above. The point of attachment of the alkylaryl group to a molecule may be via the alkyl portion and thus, preferably, the alkylaryl group is —CH₂-Ph or —CH₂CH₂-Ph. An alkylaryl group can also be referred to as “aralkyl”.

An alkylheteroaryl group can comprise any of the alkyl or heteroaryl groups discussed above. Preferably the alkylheteroaryl group is a “heteroaryl C₁₋₂₀ alkyl group”, more preferably a preferably a “heteroaryl C₁₋₁₆ alkyl group”, even more preferably a “heteroaryl C₁₋₆ alkyl group” and is a heteroaryl group as defined above bonded at any position to an alkyl group as defined above. The point of attachment of the alkylheteroaryl group to a molecule may be via the alkyl portion. An alkylheteroaryl group can also be referred to as “heteroaralkyl”.

An ether group is preferably a group OR₆ wherein R₆ can be an aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl group as defined above. In certain embodiments, R₆ can be an unsubstituted aliphatic, alicyclic or aryl. Preferably, R₆ is an alkyl group selected from methyl, ethyl or propyl. A thioether group is preferably a group SR₆ wherein R₆ is as defined above.

A silyl group is preferably a group —Si(R₇)₃, wherein each R₇ can be independently an aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl group as defined above. In certain embodiments, each R₇ is independently an unsubstituted aliphatic, alicyclic or aryl. Preferably, each R₇ is an alkyl group selected from methyl, ethyl or propyl.

A silyl ether group is preferably a group OSi(R₈)₃ wherein each R₈ can be independently an aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl group as defined above. In certain embodiments, each R₈ can be independently an unsubstituted aliphatic, alicyclic or aryl. Preferably, each R₈ is an alkyl group selected from methyl, ethyl or propyl.

A nitrile group is a group CN.

An azide group is a group —N₃.

An imine group is a group —CRNR, preferably a group —CHNR₉ wherein R₉ is an aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl group as defined above. In certain embodiments, R₉ is unsubstituted aliphatic, alicyclic or aryl. Preferably R₉ is an alkyl group selected from methyl, ethyl or propyl.

An acetylide group contains a triple bond —C≡C—R₁₀, preferably wherein R₁₀ can be an aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl group as defined above. For the purposes of the invention when R₁₀ is alkyl, the triple bond can be present at any position along the alkyl chain. In certain embodiments, R₁₀ is unsubstituted aliphatic, alicyclic or aryl. Preferably R₁₀ is methyl, ethyl, propyl or phenyl.

An amino group is preferably —NH₂, —NHR₁₁ or —N(R₁₁)₂ wherein R₁₁ can be an aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, a silylalkyl, aryl or heteroaryl group as defined above. It will be appreciated that when the amino group is N(R₁₁)₂, each R₁₁ group can be independently selected from an aliphatic, heteroaliphatic, alicyclic, heteroalicyclic a silylalkyl group, heteroaryl or an aryl group as defined above. In certain embodiments, each R₁₁ is independently an unsubstituted aliphatic, alicyclic or aryl. Preferably R₁₁ is methyl, ethyl, propyl, SiMe₃ or phenyl. Where W of the chain transfer agent is amine, the amine is preferably NH₂ or NHR₁₁.

An alkylamino group may be a group —NHR₁₁ or —N(R₁₁)₂ as defined above.

An amido group is preferably —NR₁₂C(O)— or —C(O)—NR₁₂— wherein R₁₂ can be hydrogen, an aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl group as defined above. In certain embodiments, R₁₂ is unsubstituted aliphatic, alicyclic or aryl. Preferably R₁₂ is hydrogen, methyl, ethyl, propyl or phenyl.

An ester group is preferably —OC(O)R₁₃— or —C(O)OR₁₃— wherein R₁₃ can be hydrogen, an aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl group as defined above. In certain embodiments, R₁₃ is unsubstituted aliphatic, alicyclic or aryl. Preferably R₁₃ is hydrogen, methyl, ethyl, propyl or phenyl.

A sulfoxide is preferably —SOR₁₄, a sulfonate group is preferably —OS(O)₂R₁₄, a sulfinate group is preferably —S(O)O—R₁₄, wherein R₁₄ can be hydrogen, an aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl group as defined above. In certain embodiments, R₁₄ is unsubstituted aliphatic, alicyclic or aryl. Preferably R₁₄ is hydrogen, methyl, ethyl, propyl or phenyl.

A carboxylate group is preferably OC(O)R₁₅, wherein R₁₅ can be hydrogen, an aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl group as defined above. In certain embodiments, R₁₅ is unsubstituted aliphatic, alicyclic or aryl. Preferably R₁₅ is hydrogen, methyl, ethyl, propyl, butyl (for example n-butyl, isobutyl or tert-butyl), phenyl, pentafluorophenyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl, hexadecyl, heptadecyl, octadecyl, nonadecyl, eicosyl, trifluoromethyl or adamantyl.

An acetamide is preferably MeC(O)N(R₁₆)₂ wherein R₁₆ can be hydrogen, an aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl group as defined above. In certain embodiments, R₁₆ is unsubstituted aliphatic, alicyclic or aryl. Preferably R₁₆ is hydrogen, methyl, ethyl, propyl or phenyl.

A phosphinate group is preferably a group —OP(O)(R₁₇)₂ wherein each R₁₇ is independently selected from hydrogen, or an aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl group as defined above. In certain embodiments, R₁₇ is aliphatic, alicyclic or aryl, which are optionally substituted by aliphatic, alicyclic, aryl or C₁₋₆alkoxy. Preferably R₁₇ is optionally substituted aryl or C₁₋₂₀ alkyl, more preferably phenyl optionally substituted by C₁₋₆alkoxy (preferably methoxy) or unsubstituted C₁₋₂₀alkyl (such as hexyl, octyl, decyl, dodecyl, tetradecyl, hexadecyl, stearyl).

It will be appreciated that where any of the above groups are present in a Lewis base G, one or more additional R^(G) groups may be present, as appropriate, to complete the valency. For example, in the context of an ether an additional R^(G) group may be present to give R^(G)OR₆, wherein R^(G) is hydrogen, an optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl group as defined above. Preferably, R^(G) is hydrogen or aliphatic, alicyclic or aryl.

Any of the aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, haloalkyl, alkoxy, alkylthio, alkylaryl, ether, ester, sulfoxide, sulfonate, sulfinate, carboxylate, silyl ether, imine, acetylide, amino, alkylamino, phosphinate or amido groups wherever mentioned in the definitions above, may optionally be substituted by halogen, hydroxyl, nitro, carbonate, alkoxy, aryloxy, heteroaryloxy, amino, alkylamino, imine, nitrile, acetylide, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl groups (for example, optionally substituted by halogen, hydroxyl, nitro, carbonate, alkoxy, amino, alkylamino, imine, nitrile or acetylide).

For the purposes of all aspects of the present invention, the epoxide, anhydride, lactide and lactone substrates are not limited.

The term epoxide therefore relates to any compound comprising an epoxide moiety. In preferred embodiments, the epoxides which are useful in the present invention have the following formula:

Wherein each R^(e1), R^(e2), R^(e3) and R^(e4) is independently selected from hydrogen, halogen, hydroxyl, nitro, alkoxy, aryloxy, heteroaryloxy, amino, alkylamino, imine, nitrile, acetylide, carboxylate or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl, or a polymeric species (e.g. polybis(phenol)A); or two or more of R^(e1), R^(e2), R^(e3) and R^(e4) can be taken together to form a saturated, partially saturated or unsaturated 3 to 12 membered, optionally substituted ring system, optionally containing one or more heteroatoms.

Preferred examples of epoxides for the purposes of the present invention include propylene oxide, cyclohexene oxide, substituted cyclohexene oxides (such as limonene oxide, C₁₀H₁₆O or 2-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, C₁₁H₂₂O), alkylene oxides (such as ethylene oxide and substituted ethylene oxides), substituted oxiranes (such as epichlorohydrin, 1,2-epoxybutane, glycidyl ethers), styrene oxide or substituted styrene oxides. For example, epoxides, may have the following structures:

The term anhydride relates to any compound comprising an anhydride moiety in a ring system (i.e. a cyclic anhydride). In preferred embodiments, the anhydrides which are useful in the present invention have the following formula:

Wherein m″ is 1, 2, 3, 4, 5, or 6 (preferably 1 or 2), each R^(a1), R^(a2), R^(a3) and R^(a4) is independently selected from hydrogen, halogen, hydroxyl, nitro, alkoxy, aryloxy, heteroaryloxy, amino, alkylamino, imine, nitrile, acetylide, carboxylate or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl, or a polymeric species (e.g. polybis(phenol)A); or two or more of R^(e1), R^(e2), R^(e3) and R^(e4) can be taken together to form a saturated, partially saturated or unsaturated 3 to 12 membered, optionally substituted ring system, optionally containing one or more heteroatoms, or can be taken together to form a double bond. Each Q is independently C, O, N or S, preferably C, wherein R^(a3) and R^(a4) are either present, or absent, and

can either be ═ or —, according to the valency of Q. It will be appreciated that when Q is C, and

is ═, R^(a3) and R^(a4) (or two R^(a4) on adjacent carbon atoms) are absent. Preferable anhydrides are set out below.

The term lactone relates to any cyclic compound comprising a —C(O)O— moiety in the ring. In preferred embodiments, the lactones which are useful in the present invention have the following formula:

Wherein m is 1 to 20 (e.g. 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13, 14, 15, 16, 17, 18, 19 or 20), preferably 2, 4, or 5; and R^(L1) and R^(L2) are independently selected from hydrogen, halogen, hydroxyl, nitro, alkoxy, aryloxy, heteroaryloxy, amino, alkylamino, imine, nitrile, acetylide, carboxylate or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl. Two or more of R^(L1) and R^(L2) can be taken together to form a saturated, partially saturated or unsaturated 3 to 12 membered, optionally substituted ring system, optionally containing one or more heteroatoms. When m is 2 or more, the R^(L1) and R^(L2) on each carbon atom may be the same or different. Preferably R^(L1) and R^(L2) are selected from hydrogen or alkyl. Preferably, the lactone has the following structure:

The term lactide is a cyclic compound containing two ester groups. In preferred embodiments, the lactides which are useful in the present invention have the following formula:

Wherein m′ is 1, 2, 3, 4, 5, 6, 7, 8, 9 or 10, (preferably 1 or 2, more preferably, 1) and R^(L3) and R^(L4) are independently selected from hydrogen, halogen, hydroxyl, nitro, alkoxy, aryloxy, heteroaryloxy, amino, alkylamino, imine, nitrile, acetylide, carboxylate or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl. Two or more of R^(L3) and R^(L4) can be taken together to form a saturated, partially saturated or unsaturated 3 to 12 membered, optionally substituted ring system, optionally containing one or more heteroatoms, When m′ is 2 or more, the R^(L3) and R^(L4) on each carbon atom may be the same or different or one or more R^(L3) and R^(L4) on adjacent carbon atoms can be absent, thereby forming a double or triple bond. It will be appreciated that while the compound has two moieties represented by (—CR^(L3)R^(L4))_(m), both moieties will be identical. In particularly preferred embodiments, m′ is 1, R^(L4) is H, and R^(L3) is H, hydroxyl or a C₁₋₆alkyl, preferably methyl. The stereochemistry of the moiety represented by (—CR^(L3)R^(L4))_(m), can either be the same (for example RR-lactide or SS-lactide), or different (for example, meso-lactide). The lactide may be a racemic mixture, or may be an optically pure isomer. Preferably, the lactide has the following formula:

The term “lactone and/or lactide” used herein encompasses a lactone, a lactide and a combination of a lactone and a lactide. Preferably, the term “lactone and/or lactide” means a lactone or a lactide.

Preferred optional substituents of the groups R^(e1), R^(e2), R^(e3), R^(e4), R^(a1), R^(a2), R^(a3), R^(a4), R^(L1), R^(L2), R^(L3) and R^(L4) include halogen, nitro, hydroxyl, unsubstituted aliphatic, unsubstituted heteroaliphatic unsubstituted aryl, unsubstituted heteroaryl, alkoxy, aryloxy, heteroaryloxy, amino, alkylamino, imine, nitrile, acetylide, and carboxylate.

DETAILED DESCRIPTION

In a first aspect, the present invention provides a method for preparing a block copolymer, using a single catalytic system, wherein the single catalytic system comprises a catalyst of formula (I):

Wherein:

[M] is a metal complex having at least one metal atom M coordinated by a ligand system;

M is Zn, Cr, Co, Mn, Mg, Fe, Ti, Ca, Ge, Al, Mo, W, Ru, Ni or V;

Z is absent, or is independently selected from -E-, -EX(E)-, or -EX(E)E-,

each E is independently selected from O, S or NR^(Z), wherein R^(Z) is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl;

X is C or S

R is hydrogen, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl, alkylheteroaryl, silyl or a polymer; and when Z is absent, R may additionally be selected from halide, phosphinate, azide and nitrate;

the method comprising the steps of:

-   -   d) forming a first block by polymerising a first monomer or         combination of monomers selected from the groups (i) to (iii):         -   Group (i): a lactide and/or a lactone,         -   Group (ii): an epoxide and an anhydride, or         -   Group (iii): an epoxide and carbon dioxide,     -   e) optionally contacting the catalyst of formula (I) with a         compound [Y] which is capable converting the group —Z—R, wherein         Z is absent or a group selected from -E-X(E)- or -E-X(E)E-, to a         group —Z—R wherein Z is -E-;     -   f) forming a second block by polymerising a second monomer or         combination of monomers selected from a different group (i)         to (iii) to that selected for the first monomer or combination         of monomers:         -   Group (i): a lactide and/or a lactone,         -   Group (ii): an epoxide and an anhydride, or         -   Group (iii): an epoxide and carbon dioxide,

wherein when the first monomer or combination of monomers is Group (i), Z is -E-; and wherein when the first monomer or combination of monomers is Group (ii) or Group (iii), and the second monomer or combination of monomers is Group (i), step b) is performed after step a).

It will be appreciated that the definition of the catalyst system for use in the method of the present invention is not limiting and encompasses any catalyst of formula (I), in particular any catalyst of formula (I) suitable for polymerisation of an epoxide with carbon dioxide, or an anhydride, to form a polycarbonate polyol or polyester polyol respectively.

Such known catalyst systems generally comprise a metal, and a ligand. The metal can be selected from Zn, Ni, Ru, Mo, Fe, Mn, Mo, Cr, V, Co, Ti, W, Al, Ca, Ge or Mg. In preferred embodiments, the metal is Zn, Mg, or Co, more preferably Mg or Zn. The catalyst can comprises one or more metal atoms, such as two metal atoms. The ligand can be a monodentate or poly dentate ligand, such as a bi-dentate, tri-dentate or tetradentate ligand.

In particular, the methods of the present invention can use a metal co-ordination compound comprising the following tetradentate ligands as disclosed in WO2010/028362, the contents of which are incorporated herein by reference: salen derivatives; derivatives of salan ligands; bis-2-hydroxybenzamido derivatives; derivatives of the Trost ligand; porphyrin derivatives; derivatives of tetrabenzoporphyrin ligands; derivatives of corrole ligands; phthalocyaninate derivatives; and dibenzotetramethyltetraaza[14]annulene derivatives.

The invention relates to catalysts comprising metal complexes comprising two or metal atoms complexed to one or more multidentate ligand(s) as disclosed in WO2012/037282, the contents of which are incorporated herein by reference.

The invention further encompasses the use of catalysts comprising bulky β-diiminate (BDI) ligands for example (BDI)-ZnO^(i)Pr as disclosed in Coates et al, J.A.C.S., (2001), 123, 3229-3238, the contents of which are incorporated herein by reference. An additional example of such a catalyst includes the salen Co(III)X/onium salt catalyst system as disclosed in Lu et al, J.A.C.S., (2012), 134, 17739-17745, the contents of which are incorporated herein by reference.

The invention further encompasses, and preferably relates to, catalysts comprising two metal atoms complexed to a multidentate ligand system as disclosed in WO2009/130470 and WO2013/034750, the entire contents of which are incorporated herein by reference.

Other examples of known catalyst systems for use in the method of the present invention include (BDI)Zn—OAc as disclosed in R. C. Jeske, A. M. DiCiccio, G. W. Coates, J. Am. Chem. Soc. 2007, 129, 11330-11331, (salen)Cr—Cl as disclosed in D. J. Darensbourg, R. R. Poland, C. Escobedo, Macromolecules 2012, 45, 2242-2248, (salen)M-Cl, where M is Cr, Al, Co or Mn, as disclosed in C. Robert, F. De Montigny, C. M. Thomas, Nature Comm. 2011, 2, 586, (salen)-Co—O₂CPH as disclosed in M. DiCicco, G. W. Coates, J. Am. Soc. 2011, 133, 10724-10727, (Tp-porph)Al—Cl as disclosed in T. Aida, S. Inoue, J. Am. Chem. Soc. 1985, 107, 1358-1364 and T. Aida, K. Sanuki, S. Inoue, Macromolecules 1985, 18, 1049; (sal*)MCl where M is Al, Cr or Co as disclosed in E. Hosseini Nejad, C. G. W. van Melis, T. J. Vermeer, C. E. Koning, R. Duchateau, Macromolecules, 2012, 45, 1770-1776, (Ph-salen)Cr—Cl as disclosed in E. Hosseini Nejad, A. Paoniasari, C. E. Koning, R. Duchateau, Polym. Chem, 2012, 3, 1308, the contents of all of which are incorporated herein by reference.

In preferred embodiments of the first aspect, the catalyst of formula (I) is preferably a complex of formula (IA):

wherein

R₁ and R₂ are independently hydrogen, halide, a nitro group, a nitrile group, an imine, an amine, an ether group, a silyl ether group, a thioether group, a sulfoxide group, a sulfinate group, or an acetylide group or an optionally substituted alkyl, alkenyl, alkynyl, haloalkyl, aryl, heteroaryl, alicyclic or heteroalicyclic;

R₃ is optionally substituted alkylene, alkenylene, alkynylene, heteroalkylene, heteroalkenylene, heteroalkynylene, arylene, heteroarylene or cycloalkylene, wherein alkylene, alkenylene, alkynylene, heteroalkylene, heteroalkenylene and heteroalkynylene may optionally be interrupted by aryl, heteroaryl, alicyclic or heteroalicyclic;

R₄ is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylheteroaryl or alkylaryl;

R₅ is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylheteroaryl or alkylaryl;

E₁ is C, E₂ is O, S or NH or E₁ is N and E₂ is O;

Z is absent, or is selected from -E-, -EX(E)-, or -EX(E)E-;

X is C or S;

E is —O—, —S—, or NR^(Z), wherein is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl;

R is hydrogen, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl, alkylheteroaryl, silyl or a polymer; and when Z is absent, R may additionally be selected from halide, phonsphinate, azide and nitro;

each G is independently absent or a neutral or anionic donor ligand which is a Lewis base; and

M is Zn(II), Cr(II), Co(II), Mn(II), Mg(II), Fe(II), Ti(II), Cr(III)-Z—R, Co(III)-Z—R, Mn (III)-Z—R, Fe(III)-Z—R, Ca(II), Ge(II), Al(III)-Z—R, Ti(III)-Z—R, V(III)-Z—R, Ge(IV)-(—Z—R)₂ or Ti(IV)-(—Z—R)₂.

R₁ and R₂ are independently hydrogen, halide, a nitro group, a nitrile group, an imine, an amine, an ether group, a silyl ether group, a thioether group, a sulfoxide group, a sulfinate group, or an acetylide group or optionally substituted alkyl, alkenyl, alkynyl, haloalkyl, aryl, heteroaryl, alicyclic or heteroalicyclic. R₁ and R₂ may be the same or different. R₁ and R₂ are preferably independently selected from hydrogen, tBu, Me, CF₃, phenyl, F, Cl, Br, I, NMe₂, NEt₂, NO₂, OMe, OSiEt₃, CNMe, CN or CCPh, more preferably hydrogen, OMe, Me, NO₂, halogen or tBu (e.g. hydrogen or tBu). In certain embodiments, R₂ is hydrogen and R₁ is any one of the groups defined above, preferably NO₂, halogen, tBu, OMe or Me, more preferably tBu, OMe or Me.

R₃ is a disubstituted alkyl, alkenyl, alkynyl, heteroalkyl, heteroalkenyl or heteroalkynyl group which may optionally be interrupted by an aryl, heteroaryl, alicyclic or heterolicyclic group, or may be a disubstituted aryl or cycloalkyl group which acts as a bridging group between two nitrogen centres in the catalyst of formula (IA). Thus, where R₃ is a alkylene group, such as dimethylpropylene, the R₃ group has the structure —CH₂—C(CH₃)₂—CH₂—. The definitions of the alkyl, aryl, cycloalkyl etc groups set out above therefore also relate respectively to the alkylene, arylene, cycloalkylene etc groups set out for R₃. In certain embodiments, R₃ is optionally substituted alkylene, alkenylene, alkynylene, heteroalkylene, heteroalkenylene, heteroalkynylene, arylene, heteroarylene or cycloalkylene; wherein alkylene, alkenylene, alkynylene, heteroalkylene, heteroalkenylene and heteroalkynylene may optionally be interrupted by aryl, heteroaryl, alicyclic or heteroalicyclic. In particularly preferred embodiments, R₃ is a propylene group which is optionally substituted by aliphatic (preferably C₁₋₆alkyl) or aryl groups. Preferably R₃ is ethylene, 2,2-dimethylpropylene, propylene, butylene, phenylene, cyclohexylene or biphenylene, more preferably 2,2-dimethylpropylene. When R₃ is cyclohexylene, it can be the racemic, RR— or SS— forms.

R₄ is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylheteroaryl or alkylaryl. Preferably R₄ is independently selected from hydrogen, or optionally substituted alkyl, alkenyl, alkynyl, aryl or heteroaryl. Exemplary options for R₄ include H, Me, Et, Bn, iPr, tBu or Ph. More preferably, R₄ is hydrogen.

R₅ is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylheteroaryl or alkylaryl. Preferably R₅ is independently selected from hydrogen, or optionally substituted aliphatic or aryl. More preferably, R₅ is selected from hydrogen, alkyl or aryl. Exemplary R₅ groups include hydrogen, methyl, trifluoromethyl, ethyl and phenyl (preferably hydrogen, trifluoromethyl and methyl). In particularly preferred embodiments, all instances of R₅ are hydrogen.

In certain embodiments, R₁, R₂, R₃, R₄ and R₅ are each independently optionally substituted by halogen, hydroxyl, nitro, carbonate, alkoxy, aryloxy, heteroaryloxy, amino, alkylamino, imine, nitrile, acetylide, or unsubstituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl. Preferably R₁, R₂, R₃, R₄ and R₅ are each independently optionally substituted by halogen, hydroxyl, nitro, carbonate, alkoxy, aryloxy, imine, nitrile, acetylide, unsubstituted aliphatic, unsubstituted alicyclic and unsubstituted aryl.

In certain embodiments, E₁ is C, E₂ is O, S or NH, and preferably E₂ is O. In other embodiments, E₁ is N and E₂ is O. In particularly preferred embodiments, E₁ is C and E₂ is O.

G is either present or absent. When G is not absent, it is a group which is capable of donating a lone pair of electrons (i.e. a Lewis base). In certain embodiments, G is a nitrogen containing Lewis base. Each G may independently be neutral or negatively charged. If G is negatively charged, then one or more positive counterions will be required to balance out the change of the complex. Suitable positive counterions include group 1 metal ions (Na⁺, K⁺, etc), group 2 metal ions (Mg²⁺, Ca²⁺, etc), imidazolium ions, positively charged optionally substituted heteroaryl, heteroalicyclic or heteroaliphatic groups, ammonium ions (i.e. N(R¹²)₄ ⁺), iminium ions (i.e. (R¹²)₂C═N(R¹²)₂ ⁺, such as bis(triphenylphosphine)iminium ions) or phosphonium ions (P(R¹²)₄ ⁺), wherein each R¹² is independently selected from hydrogen or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl or heteroaryl. Exemplary counterions include [H—B]⁺ wherein B is selected from triethylamine, 1,8-diazabicyclo[5.4.0]undec-7-ene and 7-methyl-1,5,7-triazabicyclo[4.4.0]dec-5-ene.

G is preferably independently selected from an optionally substituted heteroaliphatic group, an optionally substituted heteroalicyclic group, an optionally substituted heteroaryl group, a halide, hydroxide, hydride, a carboxylate, an ether, a thioether, carbene, a phosphine, a phosphine oxide, an amine, an acetamide, acetonitrile, an ester, a sulfoxide, a sulfonate and water. More preferably, G is independently selected from water, an alcohol, a substituted or unsubstituted heteroaryl (imidazole, methyl imidazole, pyridine, 4-dimethylaminopyridine, pyrrole, pyrazole, etc), an ether (dimethyl ether, diethylether, cyclic ethers, etc), a thioether, carbene, a phosphine, a phosphine oxide, a substituted or unsubstituted heteroalicyclic (morpholine, piperidine, tetrahydrofuran, tetrahydrothiophene, etc), an amine, an alkyl amine (trimethylamine, triethylamine, etc), acetonitrile, an ester (ethyl acetate, etc), an acetamide (dimethylacetamide, etc), a sulfoxide (dimethylsulfoxide, etc), a carboxylate, a hydroxide, hydride, a halide, a nitrate, a sulfonate, etc. In some embodiments, one or both instances of G is independently selected from optionally substituted heteroaryl, optionally substituted heteroaliphatic, optionally substituted heteroalicyclic, halide, hydroxide, hydride, an ether, a thioether, carbene, a phosphine, a phosphine oxide, an amine, an alkyl amine, acetonitrile, an ester, an acetamide, a sulfoxide, a carboxylate, a nitrate or a sulfonate. In certain embodiments, G may be a halide; hydroxide; hydride; water; a heteroaryl, heteroalicyclic or carboxylate group which are optionally substituted by alkyl, alkenyl, alkynyl, alkoxy, halogen, hydroxyl, nitro or nitrile. In preferred embodiments, G is independently selected from halide; water; a heteroaryl optionally substituted by alkyl (e.g. methyl, ethyl etc), alkenyl, alkynyl, alkoxy (preferably methoxy), halogen, hydroxyl, nitro or nitrile. In some embodiments, one or both instances of G is negatively charged (for example, halide). In further embodiments, one or both instances of G is an optionally substituted heteroaryl. Exemplary G groups include chloride, bromide, pyridine, methylimidazole (for example N-methyl imidazole) and dimethylaminopyridine (for example, 4-methylaminopyridine).

Preferably G is absent.

It will be appreciated that when a G group is present, the G group may be associated with a single M metal centre as shown in formula (IA), or the G group may be associated with both metal centres and form a bridge between the two metal centres.

Preferably M is Zn(II), Cr(III), Cr(II), Co(III), Co(II), Mn(III), Mn(II), Mg(II), Fe(II), Fe(III), Ca(II), Ge(II), Ti(II), Al(III), Ti(III), V(III), Ge(IV) or Ti(IV), more preferably Zn(II), Cr(III), Co(II), Mn(II), Mg(II), Fe(II) or Fe(III), and most preferably Zn(II) or Mg(II). It will be appreciated that when M is Cr(III), Co(III), Mn(III) or Fe(III), the catalyst of formula (IA) will contain an additional —Z—R group co-ordinated to the metal centre, wherein —R—R is as defined herein. It will also be appreciated that when M is Ge(IV) or Ti(IV), the catalyst of formula (IA) will contain two additional —Z—R groups co-ordinated to the metal centre, wherein —Z—R is as defined above. In certain embodiments, when M is Ge(IV) or Ti(IV), both G may be absent.

The skilled person will also appreciate that each M may be the same (for example, both M may be Mg, Zn, Fe or Co) or each M may be different and can be present in any combination (for example, Fe and Zn, Co and Zn, Mg and Fe, Co and Fe, Mg and Co, Cr and Mg, Cr and Zn, Mn and Mg, Mn and Zn, Mn and Fe, Cr and Fe, Cr and Co, Al and Mg, Al and Zn etc). When M is the same metal, it will be appreciated that each M may be in the same oxidation state (for example both M may be Co(II), Fe(II) or Fe(III)), or in a different oxidation state (for example, one M may be Co(II) and the other M may be Co(III), one M may be Fe(II) and the other M may be Fe(III), or one M may be Cr(II) and the other M may be Cr(III)).

—Z— is either absent or selected from -E-, -E-X(E)- or -E-X(E)-E-.

X is C or S, preferably C.

E is O, S, or NR^(Z).

When Z is -E-X(E)-, -E-X(E)- is preferably —O—(CO)—, —NR^(Z)—CO)—, —O—C(═NR^(Z))—, —O—C(S)—, —O—S(O)—, —NR^(Z)—S(O)— or —O—S(═NR^(Z))—.

When Z is -E-X(E)-E-, -E-X(E)-E-. is preferably —O—(CO)—O, —NR^(Z)—C(O)—O—, —NR^(Z)—C(O)—NR^(Z), —O—C(═NR^(Z))—O—, —O—C(═NR^(Z))—NR^(Z)—, —O—C(S)—O—, —O—C(O)—NR^(Z), —O—S(O)—O—, —NR^(Z)—S(O)—O—, —O—S(O)—NR^(Z).

Preferably, each occurrence of E is O.

In certain embodiments, each E is O and X is C.

Each NR^(Z) is independently H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl. Preferably NR^(Z) is hydrogen or C₁₋₆alkyl.

R is hydrogen, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl, alkylheteroaryl or silyl. Preferably, R is an optionally substituted alkyl, alkenyl, alkynyl, aryl, alkylaryl, cycloalkyl, cycloalkenyl, cycloalkynyl, heteroaryl, cycloheteroalkyl, alkylheteroaryl or silyl. More preferably, R is C₁₋₁₂alkyl, cycloalkyl or aryl (for example, methyl, ethyl, n-propyl, isopropyl, n-butyl, tert-butyl, phenyl, cyclohexyl etc).

When —Z— is absent, in addition to the above groups, R may also be a halide, phosphinate, azide or nitrate.

Preferably, R may be substituted by halogen, hydroxyl, nitro, unsubstituted aryl, unsubstituted alkyl, unsubstituted alkenyl, unsubstituted alkoxy and unsubstituted aryloxy. For example, R may be an alkyl group substituted by halogen, for instance R may be CF₃.

It will also be appreciated that R can be a polymer chain. For example, R may be a polycarbonate or a polyester.

The catalyst of formula (IA) has two or more occurrences of —Z—R, depending on the oxidation state of the metal M. Each —Z—R may be the same, or different.

The skilled person will also understand that the moiety in the group —R which is attached to the group —Z— will not be a heteroatom (for example, O, S or N) or a group C=E′, where E′ is a heteroatom (for example O, S, or N).

In particularly preferred embodiments, R₁ and R₂ are independently hydrogen, or optionally substituted alkyl, alkenyl, halogen, hydroxyl, nitro, alkoxy, aryl, heteroaryl, alkylaryl and alkylheteroaryl; R₃ is optionally substituted alkylene or arylene; R₄ is hydrogen, or optionally substituted alkyl or heteroaryl; R₅ is hydrogen or optionally substituted alkyl; E₁ is C and E₂ is O; M is Mg, Zn, Fe or Co; Z is either absent or selected from —O—R, O—C(O)—R or —OC(O)—O—R; R is optionally substituted alkyl, alkenyl, cycloalkyl, aryl, heteroaryl, alkylaryl or alkylheteroaryl; or when Z is absent, R is phosphinate or halide; G is either absent, or is selected from optionally substituted heteroaryl or halide. It will be appreciated that when G is a halogen, a counterion must be present. Preferably, the counterion is [H—B]⁺, wherein B is preferably selected from NEt₃, 1,8-diazabicyclo[5.4.0]undec-7-ene (DBU) and 7-methyl-1,5,7-triazabicyclo[4.4.0]dec-5-ene (MTBD).

Exemplary catalysts of formula (IA) are as follows:

[L¹Mg₂Cl₂(methylimidazole)],

[L₁Mg₂Cl₂(dimethylaminopyridine)],

[L₁Mg₂Br₂(dimethylaminopyridine)],

[L¹Zn₂(F₃CCOO)₂],

[L¹Zn₂(OOCC(CH₃)₃)₂],

[L¹Zn₂(OC₆H₅)₂],

[L¹Fe₂Cl₄],

[L¹Co₂(OAc)₃],

[L¹Zn₂(adamantyl carbonate)₂],

[L¹Zn₂(pentafluorobenzoate)₂],

[L¹Zn₂(diphenylphosphinate)₂],

[L¹Zn₂(bis(4-methoxy)phenyl phosphinate)₂],

[L¹Zn₂(hexanoate)₂],

[L¹Zn₂(octanoate)₂],

[L¹Zn₂(dodecanoate)₂],

[L¹Mg₂(F₃CCOO)₂],

[L¹Mg₂Br₂],

[L¹Zn₂(C₆F₅)₂],

[L¹Zn₂(C₆H₅)₂] and

[L¹Zn₂(OiPr)₂].

The compound [Y] which can be used in the first aspect of the present invention must be capable of converting the group —Z—R, wherein Z is absent or a group selected from -E-C(E)- or -E-C(E)E-, to a group —Z—R wherein Z is -E-. In other words, the compound [Y] must be capable of inserting into the bond between the metal atom in the metal complex [M] and the group —Z—R in order to switch the ligand attached to the metal atom from —R, -E-C(E)-R or E-C(E)-E-R to -E-R.

The compound [Y] may be a compound having a three, four or five membered saturated ring and at least one heteroatom selected from O, S or N. In preferred embodiments, the compound [Y] may be an epoxide, an aziridine, an episulfide, an oxetane, a thietane, an azetidine, a saturated furan, a saturated thiophene or a pyrrolidine.

In certain embodiments, the compound [Y] has the following formula:

Wherein

A is O, S or NR^(A); (preferably A is O)

j is 1, 2, or 3;

R^(A) is hydrogen, halogen, hydroxyl, alkoxy, aryloxy, heteroaryloxy, or aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl;

Each R^(A1), R^(A2), R^(A3) and R^(A4) is independently selected hydrogen, halogen, hydroxyl, nitro, alkoxy, aryloxy, heteroaryloxy, amino, alkylamino, imine, nitrile, acetylide, carboxylate or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl; or two or more of R^(A1), R^(A2), R^(A3) and R^(A4) can be taken together to form a saturated, partially saturated or unsaturated 3 to 12 membered, optionally substituted ring system, optionally containing one or more heteroatoms. For example, each R^(A1), R^(A2), R^(A3) and R^(A4) may be H; R^(A1), R^(A2) and R^(A3) may be H and one or more R^(A4) may be aryl or aliphatic, preferably phenyl or alkyl; R^(A1) and R^(A4) may be H, and R^(A2) and R^(A3) may be taken together to form a six to 10 membered carbon ring (saturated, unsaturated or partially saturated. For example, the compound [Y] may be:

Preferred optional substituents of the groups R^(A1), R^(A2), R^(A3) and R^(A4) include halogen, nitro, hydroxyl, unsubstituted aliphatic, unsubstituted heteroaliphatic unsubstituted aryl, unsubstituted heteroaryl, alkoxy, aryloxy, heteroaryloxy, amino, alkylamino, imine, nitrile, acetylide, and carboxylate.

In preferred embodiments, the compound [Y] is an epoxide. When the compound [Y] is an epoxide, it will be appreciated that it may be the same, or different, to the epoxide monomer to be polymerised. In highly preferred embodiments, the compound [Y] is an epoxide which is the same as the epoxide to be polymerised by the method of the first aspect.

The polymerisation of an epoxide and carbon dioxide has been performed in the presence of various catalysts of formula (I), for example, the catalysts described in WO2009/130470 and WO 2013/034750 (each of which are herein incorporated by reference in their entirety). The reaction between the monomers, carbon dioxide and the epoxide, at the metal atom M proceeds by the following pathway in which the carbon dioxide inserts into the bond between the metal atom and the labile ligand -E-R (represented below by —O—R) to form a carbonate group attached to the metal atom, followed by the insertion of an epoxide between the carbonate group and the metal atom, in order to regenerate the group —O—R:

The skilled person will understand that R^(P) represents the growing polymer chain and will therefore increase in size after each addition of CO₂/epoxide monomer.

The polycarbonates produced by the reaction between an epoxide and carbon dioxide in the presence of a catalyst of formula (I) may be represented as follows:

Wherein n₁ is 1 to 1,000,000, for example 10 to 100,000, such as 100 to 10,000, e.g. 10 to 1,000.

It will be understood that the moiety attached to the metal atom M will either be -E-R or -E-X(E)-R (i.e. E is O and R is R^(P)). As the copolymerisation of carbon dioxide and an epoxide is generally carried out using a vast excess of carbon dioxide (due to the low cost and availability of this reagent, and to ensure entire consumption of the epoxide monomer), the moiety attached to the metal complex [M] will predominantly be —O—C(O)—O—R once the reaction has terminated.

It has been surprisingly found that the catalysts as described in WO 2009/130470 and WO 2013/034750 are also capable of polymerising an epoxide and an anhydride. This reaction is as set out in the fourth aspect of the application below, with the catalysts defined as catalysts of formula (IA).

The reaction between the anhydride and the epoxide monomers at the metal complex [M] proceeds by the following pathway in which the anhydride inserts into the bond between the metal atom and the labile ligand -E-R (represented below by —O—R^(P)) to form an ester group attached to the metal atom, followed by the insertion of an epoxide between the ester group and the metal atom, in order to regenerate the group —O—R^(P):

R^(P) represents the growing polymer chain, and therefore increases in size upon the addition of each epoxide/anhydride monomer.

The polyesters produced by the reaction between an epoxide and an anhydride in the presence of a catalyst of formula (I) may be represented as follows:

Wherein n₂ is 1 to 1,000,000, for example 10 to 100,000, such as 100 to 10,000, e.g. 10 to 1,000.

The inventors have found that, in the copolymerisation of an epoxide and an anhydride, the moiety attached to the metal complex [M] will either be —O—C(O)—R or —O—R. When the reaction terminates, the moiety attached to the metal complex will depend on which of the monomers is in excess.

The present invention further provides the use of catalysts of formula (IA) for initiating the ring opening of lactide and/or lactone monomers. When used in this manner, it is required that the labile ligand is —Z—R is —O—R, S—R or —NR^(Z)—R.

The ring opening of a lactide and a lactone in the presence of a catalyst system having a catalyst of formula (I) may be represented as follows:

In the above schemes, n₃ and n₄ are independently selected from 1 to 10,000, for example, 1 to 5000, such as 10 to 1000.

The inventive methods described herein can therefore be used to ring open a lactide and/or a lactone in order to make dimers, trimers, tetramers, penatmers etc (i.e. when n³ or n⁴=2, 3, 4, 5) or polymers (i.e. when n³ or n⁴=1 to 10,000). This method is described in the third aspect of the present invention.

The complexes of formula (I), in particular compounds of formula (IA), retain their active centres after the initial polymerisation has proceeded to completion. In other words, the metal complex [M] at the end of the polymer chain is a “dormant” catalytic species once one or more of the initial monomer species has been used up. This means that propagation may resume upon the introduction of additional monomer(s).

In a particular embodiment of the first aspect of the invention, there is provided a method for producing a polycarbonate-polyester block copolymer, the method comprising initially polymerising carbon dioxide and an epoxide in the presence of a single catalytic system having a catalyst of formula (I) to form a polycarbonate block and, adding anhydride (and optionally further epoxide, which may be the same or different to the epoxide used to produce the first block) to the reaction mixture. This reaction may be represented as follows:

In an alternative embodiment, there is provided a method for producing a polyester-polycarbonate block copolymer, the method comprising initially polymerising an epoxide and an anhydride epoxide in the presence of a single catalytic system having a catalyst of formula (I) to form a polyester block, and subsequently adding carbon dioxide (and optionally further epoxide, which may be the same or different to the epoxide used to produce the first block) to the reaction mixture. This reaction may be represented as follows:

In both of the above reactions, it will be appreciated that further epoxide will need to be added to the reaction mixture in order to produce the second block if all of the epoxide has been consumed in the production of the first block.

As discussed above, the moiety attached to the metal complex [M] after the copolymerisation of an anhydride or carbon dioxide with an epoxide has taken place will be an ester group (—OC(O)—R) or a carbonate group (—OC(O)—O—R), respectively, if the reaction is carried out with an excess of carbon dioxide/anhydride.

The inventors have recognised that, in order to use lactides and/or lactones in the method of the first aspect, it is necessary to specifically tailor the group attached to the metal complex [M] so that ring opening polymerisation can proceed.

The inventors have found that it is possible to “convert” the moiety attached to the metal complex [M] by adding a compound [Y] to the single catalytic system comprising a catalyst of formula (I). The compound [Y] is capable converting the group —Z—R, wherein Z is absent or a group selected from -E-X(E)- or -E-X(E)E- (for example, —O—C(O)—R or —O—C(O)—O—R), to a group -E-R (for example, —O—R). The compound [Y] inserts in between the metal complex [M] and the group —R, -E-X(E)-R or -E-X(E)-E-R, thereby ensuring that the moiety attached to the metal complex [M] is -E-R.

In an alternative embodiment of the first aspect, there is provided a method for producing a polyester-polyester, or a polycarbonate-polyester block copolymer, the method comprising initially polymerising an epoxide and an anhydride, or an epoxide and carbon dioxide, using a single catalyst system having a catalyst of formula (I) to form a first polyester block or a polycarbonate block, respectively, converting the moiety attached to the metal complex [M] at the end of the polymer chain from an ester group (—OC(O)—) or a carbonate group (—OC(O)—O—), to a group -E- (for example an alkoxy group, and alkylthio group or a primary or secondary amine group) using a compound [Y], and then adding a lactide and/or a lactone. These reactions maybe represented as follows:

The skilled person will appreciate that the compound [Y] may be added after the first block has been prepared. Alternatively, it will be appreciated that if all of the epoxide is not consumed in the formation of the first block, the remaining epoxide monomer will insert into the bond between the complex [M] and the ester group —OC(O)—R or the carbonate group —O—C(O)O—R, thereby functioning as the compound [Y]. Therefore, the compound [Y] may be present in the initial reaction mixture, for example, in the form of an excess of epoxide.

The lactide and/or lactone may be added at the same time as, or after, the addition of compound [Y] to the single catalytic system.

In an alternative embodiment of the first aspect, there is provided a method for producing a polyester-polyester, or polyester-polycarbonate block copolymer, the method comprising ring opening a lactide and/or a lactone, and subsequently adding an epoxide and carbon dioxide or an epoxide and an anhydride. It will be appreciated that if the first block is prepared by ring opening of a lactide and/or a lactone, the catalyst system must contain a catalyst of formula (I), where the labile ligand —Z—R is -E-R.

It is possible that the epoxide monomer used to produce the second block may be added to the single catalytic system at the same time as the anhydride/carbon dioxide, or it may be present in the single catalytic system prior to the production of the first block.

This reaction can be represented as follows:

It will be appreciated that when the first block is prepared by ring opening a lactide and/or a lactone, a compound [Y] can be used to transform catalysts of formula (I) where —Z—R is not -E-R into catalysts where —Z—R is -E-R.

Alternatively, catalysts of formula (I) where —Z—R is —R (i.e. wherein E is absent) can be transformed into catalysts formula (I) where —Z—R is -E-R by contacting the catalyst of formula (I) with compound containing an alcohol, a thiol or a primary or secondary amine. For example, the compound may an aliphatic, heteroaliphatic, aryl, heteroaryl, alicyclic or heteroalicyclic group which is substituted by one or more (e.g. two or more) —OH, —SH, or —NHR^(Z) groups. For instance, the compound may be isopropyl alcohol, 1, 2-cyclohenanediol, 1,2-ethylene glycol, 1,2-propylene glycol, 1,3-propylene glycol, benzyl alcohol, ethanol, methanol, n-propanol, a hexose, a pentose, poly(ethyleneglycol), etc. Thus, it is possible to produce the desired catalyst for step a) of the first aspect in situ.

In certain embodiments, the method of the first aspect further comprises the step of forming a third block by polymerising a third monomer or combination of monomers selected from the groups:

-   -   Group (I): a lactide and/or a lactone;     -   Group (ii): an epoxide and an anhydride; and     -   Group (iii): an epoxide and carbon dioxide.

If Group (i) is added to the single catalytic system, the method may also comprise the step of contacting the single catalytic system with a compound [Y]. This may be done prior to, or at the same time as, contacting the single catalytic system with the third monomer or combination of monomers.

In certain embodiments, the third monomer or combination of monomers is different from the Group of monomer used to produce the first and second blocks. In other embodiments, the third monomer or combination of monomers is selected from the same group of monomer or combination of monomers used to produce the first block.

The tri-block copolymer produced may be an ABC block copolymer, i.e. each of the blocks is different. Alternatively, the tri-block copolymer may be an ABA block copolymer, i.e. when the first and the third blocks are the same.

The skilled person will also appreciate that the method according to the first aspect can also be used to produce block copolymers having four, five, six, seven, etc blocks, and that the order and identity of the blocks can be tailored accordingly. For example, the method of the first aspect may be used to produce block copolymers having alternating blocks, such as ABABA, or ABCABC. Alternatively, each of the blocks may be different.

It will be appreciated that for each of the various embodiments described for the first aspect, the single catalytic system may comprise any compound according to formula (I), and preferably comprises a compound of formula (IA).

In a second aspect, the present invention provides a method for producing a block copolymer, said block copolymer having a first and second block, using a single catalytic system, wherein the single catalytic system comprises a catalyst of formula (I):

Wherein:

[M] is a metal complex having at least one metal atom M coordinated by a ligand system;

M is Zn, Cr, Co, Mn, Mg, Fe, Ti, Ca, Ge, Al, Mo, W, Ru, Ni or V;

Z is absent, or is independently selected from -E-, -EX(E)-, or -EX(E)E-,

each E is independently selected from O, S or NR^(Z), wherein R^(Z) is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl;

X is C or S

R is hydrogen, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl, alkylheteroaryl, silyl or a polymer; and when Z is absent, R may also be selected from halide, phosphinate, azide and nitrate;

the method comprising the steps of:

-   -   c) providing a mixture comprising:         -   I. an epoxide;         -   II. a first monomer or combination of monomers selected from             a group (i) to (iii):             -   Monomer (i): a lactide and/or a lactone,             -   Monomer (ii): an anhydride, or             -   Monomer (iii): carbon dioxide, and         -   III. a second monomer or combination of monomers selected             from a different group (i) to (iii) to that selected for the             first monomer or combination of monomers:             -   Monomer (i): a lactide and/or a lactone,             -   Monomer (ii): an anhydride, or             -   Monomer (iii): carbon dioxide; and     -   d) contacting the mixture with the single catalytic system;

wherein the rate of insertion of the first monomer or combination of monomers into the bond between the metal complex [M] and the ligand —Z—R is faster than the rate of insertion of the second monomer or combination of monomers into the bond between the metal complex [M] and the ligand —Z—R.

When the first monomer or combination of monomers is Group (i), either —Z—R is -E-R, or the mixture comprises a compound [Y].

When the second monomer or combination of monomers is Group (i), the mixture comprises a compound [Y].

By “one-pot”, it is meant that the block copolymers are formed in situ, in the presence of the single catalytic system, without any sequential addition of monomer. In other words, all of the monomers are added to the reaction mixture, with the single catalyst system comprising a catalyst of formula (I), at the start of the reaction. The reaction will then selectively form block copolymers from the pool of monomers available, with exquisite selectivity.

The catalyst system can comprise a catalyst of formula (IA) as defined in the first aspect. The compound [Y] is as defined in the first aspect.

The inventors have discovered that nature of the polymer block formed will depend on the moiety at the end of the growing polymer chain attached to the metal complex [M], as well as the relative rates (r) at which each of the monomers insert into the bond between the metal complex and the ligand —Z—R. r depends on the rate constant of the monomer and the concentration of each of the components in the reaction mixture. The relative rates of insertion of the monomers can be determined by exposing one or more of the monomers to a catalyst of formula (I), and monitoring the rate at which the monomer(s) is consumed, or the rate at which polymer is produced. This can be done, for example, using quantitative spectroscopic or analytic techniques which are well known in the art, such as attenuated total reflectance IR spectroscopy (ATRIR), NMR, optical absorption spectroscopy, IR, or titration.

For example, when —Z—R is a group which is capable of polymerising a lactide and/or a lactone, an epoxide and carbon dioxide, and an epoxide and an anhydride (i.e. -E-R, in particular —O—R) the different rates of insertion may be represented as follows:

It will be appreciated that R^(P) represents the growing polymer chain, and its' structure will depend on the identity of the monomers being polymerised. It will be understood that the relative rates of insertion will affect the order in which the blocks are produced.

In certain instances, r_(anh) may be faster than r_(CO2). Alternatively, r_(CO2) may be faster than r_(anh). In certain instances, r_(lac1/lac2) is slower than both r_(anh) and r_(CO2), and faster than r_(epox′) and r_(epox″). However, r_(lac1/lac2) may be faster than r_(anh), r_(CO2), r_(epox′) and r_(epox′). For the catalysts of the present invention, r_(epox′) will be the same as, or similar to, r_(epox″), and both will be slower than r_(lac1/lac2), r_(anh) and r_(CO2).

In certain embodiments, for example, when the catalyst of formula (I) is a catalyst of formula (IA) as defined in the first aspect of the invention, r_(anh)>r_(CO2)>r_(lac1/lac2)>r_(epox′)≈r_(epox″).

In such embodiments of the second aspect, the first monomer or combination of monomers is an anhydride, and the second monomer or combination of monomers is carbon dioxide. In this case, the single catalyst system will initially selectively form a polyester block (a first block) by polymerising the epoxide and the anhydride. Once the anhydride has been consumed, the metal complex [M] at the end of the polyester chains can polymerise the carbon dioxide with any remaining epoxide to form a polycarbonate block (a second block). For a polyester block and a polycarbonate block to form, it is preferable for the initial reaction mixture to comprise a greater number of molar equivalents of epoxide than the number of molar equivalents of anhydride. In preferred embodiments, the number of molar equivalents of epoxide is 1, 2, 3, 4, 5, 6, 7, 8, 9 or 10 times greater than the number of molar equivalents of anhydride.

In an alternative of such embodiment, the first monomer or combination of monomers is an anhydride, and the second monomer or combination of monomers is a lactide and/or a lactone, in which case, the catalyst system will initially selectively form a polyester block (a first block) by polymerising the epoxide and the anhydride. The ring opening polymerisation will proceed to form a second block once the anhydride monomer has been consumed, and the moiety attached to the metal complex [M] has been converted from an ester (—OC(O)—R) to a group -E-R (preferably —O—R), by using a compound [Y]. The second block will also be a polyester, which is different to the first polyester block. For the above di-block polyester to form, it is preferable for the number of molar equivalents of epoxide, plus the number of molar equivalents of the compound [Y] to be greater than the number of molar equivalents of anhydride. The compound [Y] is preferably an epoxide (which is preferably the same as the epoxide monomer used in the formation of the first block).

In a further alternative of such embodiment, the first monomer or combination of monomers is carbon dioxide and the second monomer or combination of monomers is a lactide and/or a lactone. In this instance, the catalyst system will initially selectively form a polycarbonate block (a first block) by polymerising the epoxide and the carbon dioxide. The ring opening polymerisation can proceed (thereby forming the second block, which is a polyester) once the carbon dioxide monomer has been consumed (or removed, for example, by the application of a vacuum), and the moiety attached to the metal complex [M] has been converted from a carbonate (—OC(O)O—R) to a group -E-R (preferably —O—R), by using a compound [Y]. Preferably, the number of molar equivalents of epoxide, plus the number of molar equivalents of the compound [Y] is greater than the number of molar equivalents of carbon dioxide. The compound [Y] is preferably an epoxide (which is preferably the same as the epoxide monomer used in the formation of the first block).

In a further alternative embodiment, the first monomer or combination of monomers is carbon dioxide and the second monomer or combination of monomers is an anhydride, in which case, the single catalytic system will initially selectively form a polycarbonate block first, before forming the polyester block (the second block). The initial reaction mixture preferably comprises a greater number of molar equivalents of epoxide than the number of molar equivalents of carbon dioxide.

In a further alternative embodiment, the first monomer or combination of monomers is a lactide and/or a lactone and the second monomer or combination of monomers is carbon dioxide or an anhydride. In this case, the single catalytic system will initially selectively form a first polyester block by ring opening the lactide and/or lactone. Once the lactide and/or lactone has been consumed, the single catalytic system can polymerise the epoxide and the carbon dioxide or anhydride in order to form a second block which is a polycarbonate or a polyester (which is different to the first block), respectively.

In a further embodiment of the second aspect, the reaction mixture comprises a third monomer or combination of monomers selected from a group which is different from the first and second monomers or combination of monomers:

-   -   Monomer (i): a lactide and/or a lactone,     -   Monomer (ii): an anhydride, or     -   Monomer (iii): carbon dioxide.

Where the rate of insertion of the first and second monomers are as previously described, and where the rate of insertion of the third monomer or combination of monomers into the bond between the metal complex [M] and the ligand —Z—R is slower than both the rate of insertion of the first monomer or combination of monomers into the bond between the metal complex [M] and the ligand —Z—R, and the rate of insertion of the second monomer or combination of monomers into the bond between the metal complex [M] and the ligand —Z—R.

When the third monomer or combination of monomers is Monomer (i), the reaction mixture will comprise a compound [Y].

In certain embodiments, when the first monomer or combination of monomers is an anhydride, the second monomer or combination of monomers is carbon dioxide and the third monomer or combination of monomers is a lactide and/or a lactone, the single catalytic system will initially selectively form a first block (which is a polyester) from the pool of monomers by polymerising the anhydride and the epoxide. Once the anhydride has been consumed, the catalytic system can selectively polymerise the remaining epoxide and the carbon dioxide, thereby forming a second block, which is a polycarbonate. The ring opening of the lactide and/or lactone can proceed to form a third block once the carbon dioxide monomer has been consumed (or removed, for example by the application of a vacuum), and the moiety attached to the metal complex [M] has been converted from a carbonate (—OC(O)O—R) to a group -E-R (preferably —O—R), by using a compound [Y]. It will be appreciated that the third block will be a polyester, which is different to the first block. The number of molar equivalents of epoxide, plus the number of molar equivalents of the compound [Y] is preferably greater than the number of molar equivalents of anhydride, plus the number of molar equivalents of carbon dioxide. The compound [Y] is preferably an epoxide (which is preferably the same as the epoxide monomer used in the formation of the first and second blocks).

In an alternative embodiment, the first monomer or combination of monomers is carbon dioxide, the second monomer or combination of monomers is an anhydride and the third monomer or combination of monomers is a lactide and/or a lactone, in which case the single catalytic system will initially selectively form a first block (which is a polycarbonate) from the pool of monomers by polymerising the carbon dioxide and the epoxide. Once the carbon dioxide has been consumed (or removed, for example by application of a vacuum), the catalytic system can selectively polymerise the remaining epoxide and the anhydride, thereby forming a second block, which is a polyester. The ring opening of the lactide and/or lactone will then proceed to form a third block after the anhydride monomer has been consumed, and the moiety attached to the metal complex [M] has been converted from a carbonate (—OC(O)O—R) to a group -E-R (preferably —O—R), by using a compound [Y]. Preferably, the number of molar equivalents of epoxide, plus the number of molar equivalents of the compound [Y] is preferably greater than the number of molar equivalents of anhydride, plus the number of molar equivalents of carbon dioxide. The compound [Y] is preferably an epoxide (which is preferably the same as the epoxide monomer used in the formation of the first and second blocks).

In a further alternative embodiment, first monomer or combination of monomers is a lactide and/or a lactone, the second monomer or combination of monomers is carbon dioxide and the third monomer or combination of monomers is an anhydride, in which case the single catalytic system will initially ring open the lactide and/or lactone in order to form a polyester block (a first block). Once the lactide and/or lactone has been consumer, the single catalytic system can polymerise the epoxide and the carbon dioxide, thereby forming a polycarbonate block (a second block). After the carbon dioxide has been consumed (or removed, for example by application of a vacuum), the catalytic system can selectively polymerise the remaining epoxide and the anhydride, thereby forming a third block, which is a polyester that is different from the first block. Preferably, the number of molar equivalents of epoxide is greater than the number of molar equivalents of carbon dioxide.

In a further alternative embodiment, first monomer or combination of monomers is a lactide and/or a lactone, the second monomer or combination of monomers is an anhydride and the third monomer or combination of monomers is carbon dioxide, in which case the single catalytic system will initially ring open the lactide and/or lactone in order to form a polyester block (a first block). Once the lactide and/or lactone has been consumed, the single catalytic system can polymerise the epoxide and the anhydride, thereby forming a second block which is a polyester that is different from the first block. Once the anhydride has been consumed, the catalytic system can selectively polymerise the remaining epoxide and the carbon dioxide, thereby forming a third block, which is a polycarbonate.

In particularly preferred embodiments:

-   -   the first monomer or combination of monomers is anhydride and         the second monomer or combination of monomers is carbon dioxide;     -   the first monomer or combination of monomers is an anhydride and         the second monomer or combination of monomers is a lactide         and/or lactone;     -   the first monomer or combination of monomers is carbon dioxide         and the second monomer or combination of monomers is a lactide         and/or lactone; and     -   the first monomer or combination of monomers is anhydride, the         second monomer or combination of monomers is carbon dioxide, and         the third monomer or combination of monomers is a lactide and/or         lactone.

In each of the above embodiments of the second aspect, the anhydride is preferably phthalic anhydride, the epoxide is preferably cyclohexeneoxide, the lactide and/or lactone is preferably caprolactone and the compound [Y] is preferably cyclohexeneoxide. Furthermore, the single catalytic system preferably comprises a catalyst of formula (IA), more preferably, [L¹Zn₂(OAc)₂] or [L¹Zn₂(OiPr)₂].

In a third aspect of the invention, there is provided a method for producing a polyester, comprising contacting a lactone and/or a lactide with a catalyst system having a catalyst of formula (IA):

wherein

R₁ and R₂ are independently hydrogen, halide, a nitro group, a nitrile group, an imine, an amine, an ether group, a silyl ether group, a thioether group, a sulfoxide group, a sulfinate group, or an acetylide group or an optionally substituted alkyl, alkenyl, alkynyl, haloalkyl, aryl, heteroaryl, alicyclic or heteroalicyclic;

R₃ is optionally substituted alkylene, alkenylene, alkynylene, heteroalkylene, heteroalkenylene, heteroalkynylene, arylene, heteroarylene or cycloalkylene, wherein alkylene, alkenylene, alkynylene, heteroalkylene, heteroalkenylene and heteroalkynylene may optionally be interrupted by aryl, heteroaryl, alicyclic or heteroalicyclic;

R₄ is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylheteroaryl or alkylaryl;

R₅ is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylheteroaryl or alkylaryl;

E₁ is C, E₂ is O, S or NH or E₁ is N and E₂ is O;

R is hydrogen, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl, alkylheteroaryl silyl, or a polymer;

Z is -E-;

E is —O—, —S—, or NR^(Z), wherein is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl;

each G is independently absent or a neutral or anionic donor ligand which is a Lewis base; and

M is Zn(II), Cr(II), Co(II), Mn(II), Mg(II), Fe(II), Ti(II), Cr(III)-Z—R, Co(III)-Z—R, Mn (III)-Z—R, Fe(III)-Z—R, Ca(II), Ge(II), Al(III)-Z—R, Ti(III)-Z—R, V(III)-Z—R, Ge(IV)-(—Z—R)₂ or Ti(IV)-(—Z—R)₂.

In a fourth aspect of the invention, there is provided method for producing a polyester, comprising contacting an anhydride and an epoxide with a catalyst system having a catalyst of formula (IA):

wherein

R₁ and R₂ are independently hydrogen, halide, a nitro group, a nitrile group, an imine, an amine, an ether group, a silyl ether group, a thioether group, a sulfoxide group, a sulfinate group, or an acetylide group or an optionally substituted alkyl, alkenyl, alkynyl, haloalkyl, aryl, heteroaryl, alicyclic or heteroalicyclic;

R₃ is optionally substituted alkylene, alkenylene, alkynylene, heteroalkylene, heteroalkenylene, heteroalkynylene, arylene, heteroarylene or cycloalkylene, wherein alkylene, alkenylene, alkynylene, heteroalkylene, heteroalkenylene and heteroalkynylene may optionally be interrupted by aryl, heteroaryl, alicyclic or heteroalicyclic;

R₄ is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylheteroaryl or alkylaryl;

R₅ is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylheteroaryl or alkylaryl;

E₁ is C, E₂ is O, S or NH or E₁ is N and E₂ is O;

Z is absent, or is selected from -E-, -EX(E)-, or -EX(E)E-;

X is S or C;

E is —O—, —S—, or NR^(Z), wherein is H, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl or alkylheteroaryl;

R is hydrogen, or optionally substituted aliphatic, heteroaliphatic, alicyclic, heteroalicyclic, aryl, heteroaryl, alkylaryl, alkylheteroaryl, or silyl, or a polymer; and when Z is absent, R may additional be selected from halide, phosphinate, azide and nitrate;

each G is independently absent or a neutral or anionic donor ligand which is a Lewis base; and

M is Zn(II), Cr(II), Co(II), Mn(II), Mg(II), Fe(II), Ti(II), Cr(III)-Z—R, Co(III)-Z—R, Mn (III)-Z—R, Fe(III)-Z—R, Ca(II), Ge(II), Al(III)-Z—R, Ti(III)-Z—R, V(III)-Z—R, Ge(IV)-(—Z—R)₂ or Ti(IV)-(—Z—R)₂.

The preferred embodiments of the complex of formula (IA) described in the first aspect apply equally to the second, third and fourth aspects.

The preferred embodiments of the compound [Y] as described in the first aspect apply equally to the second aspect.

The methods of the first, second, third and fourth aspects may be carried out in the presence of a solvent. Examples of solvents useful in the first, second, third and fourth aspects include toluene, diethyl carbonate, dimethyl carbonate, dioxane, dichlorobenzene, methylene chloride, propylene carbonate, ethylene carbonate, etc.

In each of the methods of the first, second, third and fourth aspects, the catalyst system may comprise a chain transfer agent.

The chain transfer agent may be any chain transfer agent as defined in WO 2013/034750, the entire contents of which are hereby incorporated by reference. Exemplary chain transfer agents include water, an amine, an alcohol, a thiol, a phosphinate and a carboxylic acid.

The chain transfer agent may be present in a molar ratio of at least 1:1 relative to the metal complex (catalyst of formula (I)). For example, the chain transfer agent is present in a molar ratio of at least 2:1, at least 4:1, at least 8:1, at least 16:1, at least 32:1 or at least 64:1 relative to the metal complex.

The chain transfer agent may be used to control the molecular weight (M_(n)) of the polymers produced by the process of the first, second, third and fourth aspects. Preferably, the molecular weight (M_(n)) of the polymers is from about 1,000 g/mol to about 100,000 g/mol. The molecular weight of the polymers produced can be measured by Gel Permeation Chromatography (GPC) using, for example, a GPC-60 manufactured by Polymer Labs, using THF as the eluent at a flow rate of 1 ml/min on Mixed B columns, manufactured by Polymer Labs. Narrow molecular weight polystyrene standards can be used to calibrate the instrument.

The chain transfer agent may also be used to form polymers produced by the process of first, second, third and fourth aspects which are terminated by hydroxyl groups (i.e. polyol polycarbonates/polyesters). The hydroxyl terminated polymers may be used to produce other polymeric products, such as polyurethane.

In certain embodiments of the first, second, third and fourth aspects, the monomers (i.e. the epoxide, anhydride, lactide and/or lactone) may be purified, for example by distillation, such as over calcium hydride, prior to being used of the methods according to the first, second, third and fourth aspects.

The method of the first, second third and fourth aspects of the invention may be carried out at a temperature of about 0° C. to about 200° C., for example, from about 25° C. to about 140° C., such as from about 50° C. to about 140° C. preferably from about 60° C. to about 100° C. The duration of the process may be up to 168 hours preferably 1 to 24 hours.

The method of the first, second, third and fourth aspects of the invention may be carried out at low catalytic loading, for example, the catalytic loading for the process is preferably in the range of 1:1,000-100,000 catalyst:monomer, more preferably in the region of 1:1,000-50,000 catalyst:monomer, even more preferably in the region of 1:1, 1000-10,000, and most preferably in the region of 1:10,000 catalyst:monomer.

The methods of the first, second, third and fourth aspects may be carried out in the presence of a gas. For example, when the inventive methods comprise CO₂ as a reagent, the CO₂ may be present alone, or in combination with another gas, such as nitrogen. The methods may be carried out at low pressures, such as 1 atm gas (e.g. 1 atm CO₂). However, the methods may also be carried out at pressures above 1 atm, such as 40 atm gas (e.g. 40 atm CO₂).

In a fifth aspect of the invention, there is provided a polymer obtainable from the method according to the first, second, third or fourth aspects.

It will be appreciated that the various preferred features described above for formula (IA) may be present in combination mutatis mutandis.

BRIEF DESCRIPTION OF FIGURES

FIG. 1: ATR-IR analysis of PCL-PCHC formation, showing normalised peak intensities for absorptions at 694, 1738 and 1750 cm−1 against time/min.

FIG. 2: GPC traces of PCHPE-b-PCL and PCHPE block copolymer. Curves a-d correspond to entries 1-4 in Table 2, respectively.

FIG. 3: ¹H NMR spectrum (CDCl₃, 298 K) of PCHPE-PCL copolymer. The plot illustrates the formation of both POPE and PCL blocks.

FIG. 4: M_(n) and M_(w)/M_(n) vs mol % of ε-CL conversion of PCL homopolymer catalysed by [L¹Zn₂(OAc)₂]/CHO system at 80° C.

FIG. 5: Plot of In{[LA]₀/[LA]_(t)} vs time, showing a polymerisation kinetics with a first-order dependence on lactide concentration, initiated by [L¹Mg₂OAc₂]/CHO system (cat/CHO/LA=1/10/100,100° C.).

FIG. 6: ¹H NMR spectrum (CDCl₃, 298 K) of PCL-PCHC copolymer. The plot illustrates the formation of both PCHC and PCL blocks.

FIG. 7: ATR-IR analysis of “one-pot” reaction between phthalic anhydride (PA), cyclohexeneoxide (CHO), and carbon dioxide.

FIG. 8: ¹H NMR spectra for terpolymerization reaction using L¹Zn₂(OAc)₂. Spectra show that PA is fully consumed before PCHC is formed.

FIG. 9: ¹H NMR spectrum (CDCl₃, 298 K) showing formation of PCHC in the presence of ε-CL, with no formation of PCL (4.00 ppm) or ether linkages (3.45 ppm).

FIG. 10: ATR-IR analysis of “one-pot” reaction between phthalic anhydride (PA), cyclohexeneoxide (CHO) and caprolactone (ε-CL).

FIG. 11: ¹H NMR spectrum (CDCl₃, 298 K) showing formation of PCL in the presence of CHO, without polymerization of CHO (absence of (poly)ether linkage at 3.45 ppm).

FIG. 12: SEC stack plot showing the analysis of PCHC-PCL formation. The “PCHC” trace shows the analysis of an aliquot removed after 4 h, which showed 10% CHO conversion and PCHC formation, with M_(n) 530 g/mol. At this point, the CO₂ was removed leading to ε-CL ROP. After 2 h, a second aliquot was removed showing>99% conversion of ε-CL and formation of PCHC-PCL of M_(n) 2350 g/mol.

FIG. 13: Plot of changes in intensity of IR resonances where PCHC-PCL is formed by: 1) by ROCOP of CHO/CO₂, 2) removal of CO₂ and 3) ROP of CL.

FIG. 14: SEC trace showing the molecular weight distribution PCHC and purified PCL-PCHC-PCL as described in Table 14, Entry 1.

FIG. 15: ¹H NMR spectrum showing the carbonate content of crude PCL-PCHC-PCL and purified PCL-PCHC-PCL.

FIG. 16: SEC trace showing the molecular weight distribution PCHC and crude PCL-PCHC-PCL as described in Table 14, Entry 2.

FIG. 17: MALDI TOF mass spectra of PCL obtained in neat CHO in the absence of ethylene glycol.

FIG. 18: MALDI TOF mass spectra of PCL obtained in toluene in the presence of ethylene glycol.

EXAMPLES Example 1 Ring Opening Polymerisation of a Lactone and Copolymerisation of an Anhydride and an Epoxide

Previous studies have shown that complex 1 is an excellent catalyst for the copolymerization of carbon dioxide and cyclohexene oxide (CHO) to yield poly(cyclohexylene carbonate) (PCHC), with a high fidelity (>95%) of carbonate repeat units. Complex 2 was selected as a pre-catalyst from which a range of different catalysts could be prepared by reaction between the phenyl substituents and protic reagents. For example, the reaction between complex 2 and iPrOH yields the di-zinc di-i-propoxide complex, in situ, with release of benzene.

Complex 2 is capable of copolymerising CHO/CO₂, yielding PCHC with an equivalent TON and TOF to 1 (˜400, 20, respectively), and >99% of carbonate linkages in the copolymer. The copolymerization is also highly efficient, yielding 98% polymer, with just 2% cyclohexene carbonate by-product.

Catalyst 2, in combination with four equivalents of iPrOH, is an excellent catalyst system for caprolactone (ε-CL) ring-opening polymerisation (ROP), producing poly(caprolactone) (PCL) with a high TON (460)/TOF (2300 h−1), as complex 2 reacts with iPrOH in situ to form [L¹Zn₂(O^(i)Pr)₂].

The PCL has an Mn of 30,000 g/mol.

In contrast, the ROP of caprolactone does not proceed at all using catalyst 1, when ε-CL is used alone, or in combination with iso-propyl alcohol. Furthermore, exposure of the initiating system 2/^(i)PrOH and ε-CL to 1 bar pressure of CO₂ completely deactivates the catalyst and prevents any ROP occurring.

Thus, it can be seen that for ε-CL ROP alkoxide groups can initiate polymerization, whereas carbonate and carboxylate groups cannot.

Complexes 1 and 2 are also efficient catalyst for the copolymerization of CHO and phthalic anhydride (PA), yielding the polyester poly(cyclohexylene phthalic)ester (PCHPE), with a high TON (1000)/TOF (50 h⁻¹) and high proportion of ester chain linkages (>99%).

TABLE 1 Performance of Catalysts 1 and 2 for Polyester and Polycarbonate Formation Time TOF^(b)) Mn^(c)) Monomers Catalyst (h) TON^(a)) (h⁻¹) (g · mol⁻¹) PDI^(c)) CHO/CO₂ ^(d)) 1 24 439 18 6200 1.19 CHO/CO₂ ^(d)) 2 20 408 20 5035 1.08 ε-CL^(e)) 1 + iPrOH 24 — — — — ε-CL^(e)) 2 + iPrOH 0.2 460 2300 30,000 1.47 (92%) ^(a))Turn-over-number (TON) = moles monomer consumed/moles catalyst added, where moles monomer consumed is determined from the % conversion observed in the ¹H NMR spectrum of the crude polymer, ^(b))Turn-over-frequency (TOF) = TON/time (h), ^(c))Determined by size exclusion chromatography, calibrated against narrow Mw Polystyrene standards (see ESI). ^(d))Polymerization conducted at 80° C., 1 bar CO₂ pressure, 0.1 mole % catalyst in neat CHO. ^(e))Polymerization conducted at 80° C., 0.2 mole % catalyst, 0.8 mole % iPrOH (4 eq.) in neat ε-CL. f) Polymerization conducted at 100° C., 0.1 mole % catalyst in 1:9 mixture of pthalic anhydride:cyclohexene oxide, g) based on PA conversion.

The PCHPE has an M_(n) of 4000 g/mol, and a narrow PDI (1.33).

Example 2 Preparing a poly(caprolactone-co-cyclohexylene carbonate) Block Copolymer by Sequential Monomer Addition

Reacting complex 2 (as set out in Example 1), with 4 eq. iPrOH, results in a catalyst having a zinc alkoxide propagating species. ε-CL dissolved in CHO is exposed to this catalyst system, resulting in formation of PCL. After 120 minutes, 1 bar pressure of CO₂ is added to the polymerization system.

FIG. 1 illustrates the ATR-IR analysis of the polymerization. Initially, ε-CL is polymerized; this can be observed the sharp decrease in intensity of the absorptions at 694 and 1750 cm−1 (inset FIG. 1) due to ε-CL. The complete consumption of ε-CL occurs over just 20 minutes. After 120 minutes, (>5 half-life), 1 bar pressure of CO₂ is added to the polymerization system. The ATR-IR analysis shows the immediate formation of polycarbonate, as observed by the increasing intensity of signals at 1750 and 1738 cm⁻¹.

The polymerization was stopped after 24 h, the only product was poly(caprolactone-co-cyclohexylene carbonate) PCL-PCHC by GPC. The TON and TOF for the carbonate block formation are 460 and 23 h⁻¹, respectively and the carbonate block shows a very high fidelity of carbonate repeat units(>99%).

The block copolymer has Mn of 5170 g/mol, PDI=1.27. Analysis of the integrals for the PCHC vs PCL blocks, in the ¹H NMR spectrum, shows an approximate composition of 3:1, PCHC:PCL, which matches well with the composition predicted on the basis of stoichiometry (3.5:1).

Example 3 Preparing a poly(caprolactone-co-cyclohexylene carbonate) Block Copolymer by Sequential Monomer Addition

Cyclohexene oxide (2.2 mL, 21.5 mmol), ε-caprolactone (277 μL, 2.5 mmol) and complex 1 (20 mg, 25.0 μmol) were added to a Schlenk tube. The vessel was heated at 353 K, under N₂, for 1 h then de-gassed and 1 bar of CO₂ was added. The vessel was heated for 20 h. A sample of the crude product was analysed by ¹H NMR spectroscopy to determine the conversion and selectivity. Any unreacted monomers were removed, in vacuo, to yield the product as a white powder. M_(n)=4,810, PDI=1.28.

Example 4 Production of Di-Block and Tri-Block Copolymers

It can be seen from Example 2 that catalyst 2 can selectively polymerize ε-CL, in the presence of CHO, to produce PCL with good control of the M_(n). Removal of an aliquot from the polymerization after 120 mins, shows complete consumption of the ε-CL monomer and formation of PCL of M_(n) 6950 g/mol (PDI: 1.51).

The zinc-alkoxide polymer chain end can be further reacted with 50 eq. of phthalic anhydride (vs. 800 equivalents of CHO) to produce a block copolyester (PCL-CHPE). Removal of an aliquot from the reaction mixture after 400 mins shows the complete consumption of PA has occurred yielding a diblock copolyester with M_(n) 7360 g/mol (PDI: 1.62). Using an excess of CHO ensures that the growing polymer chain end is a zinc alkoxide species (vs. a zinc carboxylate which would be formed if excess PA were applied). This zinc alkoxide species was reacted with a further 200 equivalents of ε-CL to produce an ABA type triblock copolyester (PCL-PCHPE-PCL). The triblock copolymer has an Mn 12680 g/mol (PDI: 1.70).

An ABC type block copolyester carbonate is produced by reacting ε-CL with catalyst 2/iPrOH catalyst system, in CHO, to produce a zinc alkoxide chain terminated PCL dissolved in CHO. This PCL is then reacted with 50 eq. of PA, and the zinc alkoxide species initiates the copolymerization of CHO and PA. Because CHO is present in excess and the reaction is run to complete consumption of PA, the growing polymer chain is terminated by a zinc alkoxide species. The diblock polymer is then exposed to 1 bar pressure of carbon dioxide, and the copolymerization of carbon dioxide and CHO progresses to form a PCL-PCHPE-PCHC, an ABC type copolymer.

Example 5 Production of Di-Block Using Complex 1

Complex 1 (10.0 mg, 1.25×10⁻² mmol), phthalic anhydride (37.0 mg, 0.25 mmol) and ε-CL (210.0 μL, 1.88 mmol) were dissolved in CHO (505.0 μL, 5.00 mmol) under N₂ protection in a screw vial charged with a stir bar. The mixture was then heated to 100° C. and left to react under inert atmosphere for 2 h. The relative molar ratio of [Zinc cat.]/[CHO]/[PA]/[ε-CL] were as described in Table 2. The obtained block copolymers were precipitated using cold MeOH.

TABLE 2 Synthesis of PCHPE-b-PCL from a mixed monomer feedstock of CHO, PA and ε-CL. Entry [cat.]/[CHO]/[PA]/[ε-CL] TOF of PA (h⁻¹) M_(n) (kDa) M_(w)/M_(n) 1 1/500/20/100 ~13 12.2 1.42 2 1/500/20/150 ~13 15.8 1.43 3 1/500/20/200 ~13 18.7 1.57 4 1/500/10/150 ~10 22.5 1.46 5 1/500/40/150 ~14 28.0 1.52 3.9 1.03

FIG. 2 shows GPC traces of PCHPE-b-PCL and PCHPE blocks. Curves a-d correspond to entries 1-4 in Table 2, respectively.

FIG. 3 shows ¹H NMR spectrum (CDCl₃, 298 K) of the PCHPE-PCL copolymer. The plot illustrates the formation of both PCHPE and PCL blocks.

Example 6 Ring Opening of Cyclic Esters

The following reactions demonstrate the ring opening of lactides and lactones using the catalysts of the invention.

TABLE 3 Polyester formation via ROP of cyclic esters. Mn^(b) Mono- cat./^(i)PA/ T Time Conv.^(a) (g · X mer M (° C.) (h) (%) mol⁻¹) PDI^(b) OAc ε-CL 1/4/500 80 2 h 30 0 — — OAc rac-LA 1/4/500 80 24 h 0 — — C₆H₅ ε-CL^(c) 1/4/500 80 <10 mn 91.7 29970 1.47 C₆H₅ ε-CL 1/4/500 r.t. 23 h^(e) >99 41480 1.40 C₆H₅ rac-LA^(d) 1/4/200 80 15 h^(e) >99 12585 1.30 C₆H₅ rac-LA 1/4/200 r.t. 2 h 96.6 11125 1.16 C₆H₅ rac-LA 1/-/200 r.t. 2 h 92.6 28185 1.49 Reaction conditions: [M]₀ = 1M, DCM as solvent; ^(a)Determined by ¹H NMR spectroscopy; ^(b)Determined by GPC with polystyrene standards; ^(c)neat, ε-CL as solvent; ^(d)toluene as solvent; ^(e)non-optimized time.

Example 7 Ring Opening of Cyclic Esters Initiated by Complex 1/Epoxide System

The following reactions demonstrate the ring opening of lactides and lactones using the catalysts of the invention in the presence of epoxide.

i. Controlled Polymerization of ε-CL Initiated by Complex1/Epoxide System

Cyclohexene oxide (2.55 mL, 25 mmol), ε-caprolactone (0.831 mL, 7.5 mmol) and L¹Zn₂OAc₂ (10 mg, 0.0125 mmol) were added to a Schlenk tube. The vessel was heated at 80° C. as described in Table 4. The unreacted monomers were removed in vacuo.

TABLE 4 Polyester formation via ROP of cyclic esters Time Conv.^(a) Mn^(b) (min) (%) (g · mol⁻¹) PDI^(b) 20 9.8 6,000 1.23 30 26.5 17,500 1.25 34 33.3 19,100 1.19 38 53.8 35,900 1.28 42 66.5 44,500 1.38 46 86 59,000 1.33 56 93.0 65,600 1.34 Reaction conditions: Mixed monomer as solvent, 80° C., L¹Zn₂(OAc)₂ as catalyst, cat/CHO/eCL = 1/2000/600; ^(a)Conversion of monomer determined by ¹H NMR spectroscopy; ^(b)Experimental M_(n) determined by GPC in THF, using polystyrene standards and times correction factor 0.54 for PLA to determine absolute molecular weight.

FIG. 4 shows M_(n) and M_(w)/M_(n) vs mol % of ε-CL conversion of PCL homopolymer catalyzed by [L¹Zn₂(OAc)₂]/CHO system at 80° C.

ii. Variation of Ratio Catalyst/Epoxide for ε-CL ROP.

L¹Zn₂OAc₂ (15 mg, 0.0188 mmol), cyclohexene oxide, ε-caprolactone and toluene were added to a Schlenk tube (molar ratio cat/CHO/ε-CL as described in Table 5). The vessel was heated at 80° C. as described in Table 5. The unreacted monomers were removed in vacuo.

TABLE 5 eCL polymerisation initiated by catalyst/epoxide systems cat./CHO/ Temp. Time Conv^(a) M_(n) ^(b) Cat eCL (° C.) Conc. (h) (%) (g/mol) PDI^(d) L¹Zn₂OAc₂ 1/0/100 80 1M 5 0 — — L¹Zn₂OAc₂ 1/5/100 80 1M 5 88 11500 1.41 L¹Zn₂OAc₂ 1/10/100 80 1M 5 86 10500 1.25 L¹Zn₂OAc₂ 1/20/100 80 1M 5 88 8300 1.36 L¹Zn₂OAc₂ 1/50/100 80 1M 5 87 7300 1.31 L¹Mg₂OAc₂ 1/10/100 80 1M 5 100 8150 1.25 L¹Mg₂OAc₂ 1/20/100 80 1M 5 100 6300 1.66 L¹Mg₂OAc₂ 1/50/100 80 1M 5 93 4500 1.41 ^(a)Conversion of monomer determined by ¹H NMR spectroscopy; ^(b)Experimental M_(n) determined by GPC in THF, using polystyrene standards and times correction factor 0.56 for eCL to determine absolute molecular weight; ^(c)Calculated M_(n) value obtained from the relation [eCL]/[cat.] × conv × 114/2 (Assuming two polymer chains formed per catalyst); ^(d)M_(w)/M_(n); ^(e)Calculated M_(n) value obtained from the relation [eCL]/[cat.] × conv × 114

iii. Polymerization of Rac-Lactide Initiated by Catalyst/Epoxide Systems

L¹Zn₂OAc₂ (15 mg, 0.0188 mmol), cyclohexene oxide, rac-lactide and toluene were added to a Schlenk tube (molar ratio cat/CHO/LA as described in Table 6). The vessel was heated at 80° C. as described in Table 6. The unreacted monomers were removed in vacuo.

TABLE 6 Polymerization of rac-lactide initiated by catalyst/epoxide systems cat./CHO/ Temp. Time Conv^(a) M_(n) ^(b) Cat. LA (° C.) Conc. (h) (%) (g/mol) PDI^(d) L¹Zn₂OAc₂ 1/10/100 80 1M 5 31 3700 1.26 L¹Zn₂OAc₂ 1/10/100 100 1M 5 97 4100 2.07 L¹Zn₂OAc₂ 1/0/100 100 1M 5 0 — — L¹Zn₂OAc₂ 1/1/100 100 1M 5 3.4 210 1.21 L¹Zn₂OAc₂ 1/2/100 100 1M 5 25 1150 1.20 L¹Zn₂OAc₂ 1/5/100 100 1M 5 44 3500 1.25 L¹Zn₂OAc₂ 1/20/100 100 1M 5 98 6900 1.33 L¹Mg₂OAc₂ 1/2/100 100 1M 2 6 260 1.00 L¹Mg₂OAc₂ 1/5/100 100 1M 2 91 2800 1.95 L¹Mg₂OAc₂ 1/20/100 100 1M 2 98 3100 1.80 L¹Mg₂OAc₂ 1/50/100 100 1M 2 78 2400 1.29 ^(a)Conversion of monomer determined by ¹H NMR spectroscopy; ^(b)Experimental M_(n) determined by GPC in THF, using polystyrene standards and times correction factor 0.58 for LA to determine absolute molecular weight; ^(c) M_(w)/M_(n.)

FIG. 5 features a plot of In{[LA]₀/[LA]_(t)} vs time showing a polymerisation kinetics with a first-order dependence on lactide concentration, initiated by L¹Mg₂OAc₂/CHO system (cat/CHO/LA=1/10/100,100° C.).

Example 8 Copolymerisation of and Epoxide and an Anhydride

The following reactions demonstrate the copolymerisation of and epoxide and an anhydride using the catalysts of the invention.

TABLE 7 Polyester synthesis via CHO/anhydride copolymerization. CHO/anhydrie T Time Conv. % Mn^(c) Catalyst (eq./eq.) Solvent (° C.) (h) (%)^(a,b) polyesters^(b) (g/mol) PDI^(c) L¹Zn₂(OAc)₂ CHO/MA Toluene 100 18 92 67 12700, 1.09, 100/100 [M]₀ = 2.4M 4330 1.03 L¹Zn₂(OAc)₂ CHO/PA Toluene 100 22 27 90 5100, 1.07 100/100 [M]₀ = 1.25M 2000 1.07 L¹Zn₂(OAc)₂ CHO/PA neat 100  20^(d) >99^(e)  >99 4000 1.33 800/100 L¹Mg₂(OAc)₂ CHO/PA neat 100  6 52 88 800/100 L¹Mg₂(OAc)₂ CHO/PA Toluene 100/100 [M]₀ = 2.5M 100 22 19 83 2570 1.20 L¹Mg₂(OAc)₂ CHO/PA neat 100  1  97^(e) >99 12670, 800/100 5470 ^(a)Determined by ¹H NMR spectroscopy; ^(b)Estimated on CHO consumption, ^(c)Determined by GPC with polystyrene standards; ^(d)Non-optimized time; ^(e)Estimated on PA consumption.

TABLE 8 Polyester synthesis via styrene oxide (SO)/anhydride copolymerization. SO/ % anhydrie Time Conv. poly- Mn^(c) Catalyst (eq./eq.) (h) (%)^(a,b) mer^(b) (g/mol) PDI^(c) L¹Zn₂(OAc)₂ SO/MA 16^(d) >95 81 3400 1.90 200/200 L¹Zn₂(OAc)₂ SO/MA  6^(e) >95 74 2980 1.51 500/500 L¹Zn₂(OAc)₂ SO/PA 22^(d) >95 77 2340 1.49 200/200 Reaction conditions: reaction in toluene, 100° C., [M]₀ = 2.5M, ^(a)Determined by ¹H NMR spectroscopy; ^(b)Estimated on SO consumption, ^(c)Determined by GPC with polystyrene standards; ^(d)Non-optimized time; ^(e)Monitored by ATR-IR.

Example 9 Synthesis of Polyester-Polycarbonate Block Polymers

PCL-PCHC

TABLE 9 PCL-PCHC via step polymerization procedure. ε-CL CHO ε-CL/ Cat Co-cat t₁ conv. t₂ conv. TOF CHO (eq.) (eq.) (h) (%)^(a) (h) (%)^(a) TON (h⁻¹) 500/500 2 iPA 0.5 94 20 23.2 115 5.8 (4 eq) 100/900 2 iPA 3 94 16 34.4 310 19.4 (4 eq) 100/90 2 iPA 2 93 16 66.5 698 37.4 (4 eq) 100/900 2 iPA 2 — 20 51.3 461 23.1 (4 eq) 100/900 1 — 1 >99  21 53 477 22.7 Reaction conditions: L¹Zn₂Ph₂ (1 eq.) in the presence of iPA (4 eq.), 80° C., desired time, neat (monomer mix as solvent), ^(a)Determined by ¹H NMR spectroscopy.

FIG. 6: ¹H NMR spectrum (CDCl₃, 298 K) of PCL-PCHC copolymer. The plot illustrates the formation of both PCHC and PCL blocks when initiated by cat 1 (Table 9, entry 5).

TABLE 10 PCL-b-PCHC bloc polymer characterization. Mn^(a) % Mn^(a) % E-CL/ (g · poly- (g · poly- CHO mol⁻¹) PDI^(a) carbonate^(b) mol⁻¹) PDI^(a) carbonate^(b) 500/500 20782 1.43 8.6 100/900 4808 1.65 57 7572 1.16 30.5 100/900 4355 1.34 71 100/900 5170 1.27 76 100/900 4810 1.38 74 ^(a)Determined by GPC with polystyrene standards, ^(b)Determined by ¹H NMR spectroscopy by comparison of PCL and PCHC signals, respectively.

PE-PCHC (“One-Pot” Procedure)

TABLE 11 Polyester-polycarbonate bloc polymers obtained via one-pot polymerization procedure. ε-CL/ CHO % % CHO t conv. poly- poly- TOF (eq.) (h) (%)^(a) mer^(a) carbonate^(a) TON (h⁻¹) Mn^(b) PDI^(b) 100/900 21.8 15 81 75 134 6.1 3965 1.33 200/2000 22.2 18 91 96 362 16.5 4290 1.12 Reaction conditions: L¹Zn₂(OAc)₂ (1 eq.), 1 atm CO₂, 100° C., desired time, neat (CHO as solvent), ^(a)Determined by ¹H NMR spectroscopy, ^(b)Determined by GPC with polystyrene standards.

The second reaction in Table 11 was monitored by ATR-IR spectroscopy (see FIG. 7). FIG. 7 shows that anhydride is consumed as the polyester first block is produced.

Polyester formation terminates and polycarbonate second block formation begins once all anhydride monomer has been consumed.

FIG. 8 features ¹H NMR spectra for the terpolymerization reaction using the complex L¹Zn₂(OAc)₂ Reaction conditions: 1:100:800. Cat:PA:CHO, 100° C. under 1 bar CO₂. Spectra show that PA is fully consumed before PCHC is formed. Thus, aliquot after 4 h shows almost complete consumption of PA (by 1H NMR spectroscopy) and no formation of PCHC. At the end of the reaction (24 h), aliquot show formation of PCHC.

Example 9 Preparation Polymers from Epoxide, Carbon Dioxide, Anhydride and Lactone Monomers

TABLE 12 Polyester, polycarbonate and polycarbonate-polyester block copolymers obtained via one-pot polymerization procedure T t Conv. Mn CHO ε-CL CO₂ PA (° C.) (h) (%) (g/mol) PDI 900 100 1 atm. — 80 15 h 12.4 1040 1.08 400 200 — 50 100 10 h Full 8140 2.00 20 200 — — 80  2 h Full 21040 1.41

Formation of PCHC in the presence of ε-CL: Cyclohexene oxide (1.1 mL, 10.75 mmol), ε-caprolactone (138.6 μL, 1.2 mmol) and L¹Zn₂OAc₂ (10 mg, 0.012 mmol) were added to a Schlenk tube. The vessel was degassed then CO₂ was added and let under stirring for 30 mn at r.t. The vessel was then heated at 80° C. under CO₂ atmosphere (1 atm.) for 15 h. The unreacted monomers were removed in vacuo (Mn=1040 g/mol, PDI=1.08).

FIG. 9: ¹H NMR spectrum (CDCl₃, 298 K) showing formation of PCHC in the presence of ε-CL, with no formation of PCL (4.00 ppm) or ether linkages (3.45 ppm) (Table 12, Entry 1).

PCHPE-PCL formation: Cyclohexene oxide (1 mL, 10.0 mmol), ε-caprolactone (554 μL, 5.0 mmol), phtallic anhydride (185.2 mg, 0.625 mmol) and L¹Zn₂OAc₂ (20 mg, 0.025 mmol) were added to a Schlenk tube. The vessel was heated at 100° C. under stirring for 10 h (monitored by ATR-IR). The unreacted monomers were removed in vacuo (Mn=8140 g/mol, PDI=2.00).

FIG. 10 shows an ATR-IR trace for PCHPE-PCL formation. This figure shows that the anhydride is consumed as the polyester block forms. When all of the anhydride is consumed, ring opening of the lactone occurs.

PCL formation (in the presence of 10 mol % of CHO): Cyclohexene oxide (25 μL, 0.25 mmol), ε-caprolactone (277 μL, 2.5 mmol) and L¹Zn₂OAc₂ (10 mg, 0.0125 mmol) were added to a Schlenk tube. The vessel was heated at 80° C. under stirring for 2 h. The unreacted monomers were removed in vacuo (Mn=21040 g/mol, PDI=1.41).

FIG. 11 is a ¹H NMR spectrum (CDCl₃, 298 K) showing formation of PCL in the presence of CHO, without polymerization of CHO (absence of (poly)ether linkage at 3.45 ppm).

Example 10 Preparing a poly(cyclohexylene carbonate-co-caprolactone) Block Copolymer by Sequential Monomer Addition

-   -   A) Cyclohexene oxide (2.3 mL, 22.5 mmol), ε-caprolactone (277         μL, 2.5 mmol), and 1 (40 mg, 50.0 μmol) were added to a Schlenk         tube. The vessel was degassed at 298 K, then CO₂ was added. The         vessel was left under a CO₂ atmosphere, at 298 K, for a few         minutes and was then heated to 353 K, with continuous reaction         stirring, for 3.5 h. Then, the CO₂ was removed from the reaction         via 6 vacuum-nitrogen cycles, over a period of 15 min. The         vessel was maintained at 353 K for 3 h. A sample of the crude         product was analysed by ¹H NMR spectroscopy to determine the         conversion and selectivity. Any unreacted monomers were removed,         in vacuo, to yield the product as an oily white wax. M_(n)=3,490         g/mol, PDI=1.48.     -   B) Cyclohexene oxide (2.3 mL, 22.5 mmol), ε-caprolactone (277         μL, 2.5 mmol), and 1 (40 mg, 50.0 μmol) were added to a Schlenk         tube. The vessel was degassed at 298 K, then CO₂ was added. The         vessel was left under a CO₂ atmosphere, at 298 K, for a few         minutes and was then heated to 353 K, with continuous reaction         stirring, for 4 h. Then, the CO₂ was removed from the reaction         via 6 vacuum-nitrogen cycles, over a period of 15 min. The         vessel was maintained at 353 K for 2 h. A sample of the crude         product was analysed by ¹H NMR spectroscopy to determine the         conversion and selectivity. Any unreacted monomers were removed,         in vacuo, to yield the product as an oily white wax. M_(n)=2,349         g/mol, PDI=1.49.

FIG. 12 features a SEC stack plot showing the analysis of PCHC-PCL formation according to the conditions described in example 10-B. The “PCHC” trace shows the analysis of an aliquot removed after 4 h, which showed 10% CHO conversion and PCHC formation, with M_(n) 530 g/mol. At this point, the CO₂ was removed leading to CL ROP. After 2 h, a second aliquot was removed was >99% conversion of CL and formation of PCHC-PCL of M_(n) 2350 g/mol.

FIG. 13 shows changes in intensity of IR resonances where PCHC-PCL is formed by: 1) by ROCOP (ring opening copolymerisation) of CHO/CO₂, 2) removal of CO₂ and 3) ROP of CL.

Example 9 Use of Various Epoxides as Switch Reagent for PCL Production

LZn₂(OAc)₂ (1 eq), ε-caprolactone (200 eq), and epoxide (800 eq) were added to a schlenk tube. The mixture was heated to 80° C. for 3 hours. After 3 hours a NMR aliquot was taken to determine conversion and the excess epoxide was removed by vacuum. The polymer was precipitated from THF by methanol.

TABLE 13 Ring-opening polymerization of ε-CL initiated by a catalyst/epoxide system^(a) Conversion^(a) Mn^(b) Cat/Epoxide/e-CL Epoxide Solvent (%) (g/mol) PDI^(b) 1/800/200 SO Neat^(c) 99 5336 1.28 1/800/200 VCHO Neat^(c) 90 9486 1.4 1/10/100 SO Toluene 99 21040 1.6 [e-CL] = 1M 1/10/100 VCHO Toluene 90 13470 1.5 [e-CL] = 1M ^(a)Reaction conditions: 80° C., 3 hr; ^(b)Determined by ¹H NMR spectroscopy; ^(c)Determined by GPC calibrated with polystyrene standards; ^(c)Mixed epoxide used as solvent. VCHO = 4-vinylcyclohexene oxide; SO = styrene oxide.

Example 10 Formation of Triblock PCL-PCHC-PCL

L¹Zn₂(TFA)₂ and CHO were added to a Schlenk tube. The cyclohexene oxide was degassed before being left to stir under 1 atm of CO₂ at 80° C. for 16 h. The carbon dioxide was removed and replaced with nitrogen. Toluene was added to dissolve the PCHC, the desired quantity of ε-caprolactone was then added. Upon completion, the solvent was removed by vacuum and the polymer precipitated from THF by the addition of excess methanol.

TABLE 14 Formation of triblock PCL-PCHC-PCL Conversion^(b) Mn (PDI)^(c) CHO ε-CL (%) (g/mol) Entry (eq.) (eq.) [ε-CL]^(a) CHO ε-CL PCHC PCL-PCHC-PCL^(d) 1 1000 400 5 32 100 7,697 (1.12) 22,165 (1.78)  29,313 (1.53)^(e) 2 1000 400 1 36 87 5,644 (1.09) 15,000 (1.28) Reaction conditions: i): L¹Zn₂(TFA)₂, 18 h, 1 atm CO₂, 80° C.; ii): addition of toluene and ε-CL, 3 h, N₂ ^(a)Concentration of ε-CL in toluene; ^(b)Determined by ¹H NMR spectroscopy; ^(c)Determined by GPC calibrated with polystyrene standards, ^(d)Crude polymer before purification, ^(e)after purification THF/methanol. TFA = trifuoroacetate (OCOCF₃).

FIG. 14 shows an SEC trace showing the molecular weight distribution PCHC and purified PCL-PCHC-PCL as described in Table 14, Entry 1.

FIG. 15 shows the ¹H NMR spectrum showing the carbonate content of crude PCL-PCHC-PCL and purified PCL-PCHC-PCL. There is no significant difference in relative intensities (carbonate content) consistent with block copolymer formation.

FIG. 16 shows an SEC trace showing the molecular weight distribution PCHC and crude PCL-PCHC-PCL as described in Table 14, Entry 2.

Example 11 ε-CL Polymerization in the Presence of Chain Transfer Agent (CTA)

e-CL polymerization with CHO as solvent in the presence of ethylene glycol (EG): Catalyst, cyclohexene oxide (1000 eq), ε-caprolactone (200 eq) and ethylene glycol (10 eq) were added to a Schlenk tube. The mixture was heated to 80° C. for 2 hours and then, the excess cyclohexene oxide was removed by vacuum. The polymer was precipitated from THF by methanol.

e-CL polymerization with toluene as solvent in the presence of ethylene glycol (EG): Catalyst, cyclohexene oxide (40 eq), ε-caprolactone (400 eq), ethylene glycol (30 eq) and toluene were added to a Schlenk tube. The mixture was heated to 80° C. for 2 hours. After 2 hours the excess cyclohexene oxide removed by vacuum. The polymer was precipitated from THF by methanol.

TABLE 15 Polymerization of e-CL in the presence of CTA. ε-CL CHO EG [e-CL]^(a) Conv.^(b) Entry (eq.) (eq.) (eq.) (mol/L) (%) M_(n(exp)) ^(c) PDI^(c) P10 100 1000 — — 100 2779 1.36 P14 200 1000 10 — 100 4272 1.26 P17 400 20 10 5 100 4319 1.30 P24 200 1000 30 — 100 9069 1.35 P29 400 10 30 5 93 2754 1.18 Reaction conditions: 80° C., 2 h; ^(a)concentration of ε-CL in toluene; ^(b)Determined by ¹H NMR spectroscopy; d) determined by GPC calibrated with polystyrene standards.

FIG. 17 shows a MALDI TOF mass spectra of PCL obtained in neat CHO in the absence of EG (Table 15, P10). Polyol series calculated for [(C₆H₁₀O₂)_(n)+C₆H₁₂O₂+K]⁺=[(114.07)_(n)+116.16+39.1]⁺

FIG. 18 shows a MALDI TOF mass spectra of PCL obtained in toluene in the presence of EG (Table 15, P29). Square series calculated for [(C₆H₁₀O₂)_(n)+C₂H₆O₂+K]⁺=[(114.07)_(n)+63.04+39.1]⁺; circular series calculated for [(C₆H₁₀O₂)_(n)+C₆H₁₂O₂+K]⁺=[(114.07)_(n)+116.16+39.1]⁺. 

The invention claimed is:
 1. A method for producing a block copolymer, said block copolymer having a first and second block, using a single catalytic system, wherein the single catalytic system comprises a catalyst of formula (I):

Wherein: [M] is a metal complex having at least one metal atom M coordinated by a ligand system; M is Zn, Cr, Co, Mn, Mg, Fe, Ti, Ca, Ge, Al, Mo, W, Ru, Ni, or V; Z is absent, or is independently selected from -E-, -EX(E)-, or EX(E)E-; X is C or S; each E is independently selected from O, S, or NR^(Z), wherein R^(Z) is H, optionally substituted aliphatic, optionally substituted heteroaliphatic, optionally substituted alicyclic, optionally substituted heteroalicyclic, optionally substituted aryl, optionally substituted heteroaryl, optionally substituted alkylaryl, or optionally substituted alkylheteroaryl; R is hydrogen, optionally substituted aliphatic, optionally substituted heteroaliphatic, optionally substituted alicyclic, optionally substituted heteroalicyclic, optionally substituted aryl, optionally substituted heteroaryl, optionally substituted alkylaryl, optionally substituted alkylheteroaryl, silyl, or a polymer; and when Z is absent, R may additionally be selected from halide, phosphinate, azide, or nitro; the method comprising the steps of: a) providing a mixture comprising: i. an epoxide; ii. a first monomer or combination of monomers selected from a group (i) to (iii): Monomer (i): a lactide and/or a lactone, Monomer (ii): an anhydride, or Monomer (iii): carbon dioxide, and iii. a second monomer or combination of monomers selected from a different group (i) to (iii) to that selected for the first monomer or combination of monomers: Monomer (i): a lactide and/or a lactone, Monomer (ii): an anhydride, or Monomer (iii): carbon dioxide; and b) contacting the mixture with the single catalytic system; wherein the rate of insertion of the first monomer or combination of monomers into the bond between the metal complex [M] and the ligand —Z—R is faster than the rate of insertion of the second monomer or combination of monomers into the bond between the metal complex [M] and the ligand —Z—R; wherein when the first monomer or combination of monomers is Group (i), either —Z—R is -E-R, or the mixture comprises a compound [Y], wherein when the second monomer or combination of monomers is Group (i), the mixture comprises a compound [Y]; and wherein compound [Y] is capable of converting the group —Z—R, wherein Z is absent or a group selected from -E-X(E)- or -E-X(E)E-, to a group —Z—R wherein Z is -E-.
 2. The method according to claim 1, wherein the mixture further comprises a third monomer or combination of monomers selected from a group which is different from the first and second monomers or combination of monomers: Monomer (i): a lactide and/or a lactone, Monomer (ii): an anhydride, or Monomer (iii): carbon dioxide; wherein the rate of insertion of the first and second monomers are as claimed in claim 1, and wherein the rate of insertion of the third monomer or combination of monomers into the bond between the metal complex [M] and the ligand —Z—R is slower than the rate of insertion of the first and second monomers or combination of monomers into the bond between the metal complex [M] and the ligand —Z—R; and wherein when the third monomer or combination of monomers is Monomer (i), the reaction mixture comprises a compound [Y].
 3. The method according to claim 1, wherein the compound [Y] is a compound having a three, four, or five membered saturated ring and at least one heteroatom selected from O, S, or N.
 4. The method according to claim 1, wherein the catalyst has the following formula:

wherein R₁ and R₂ are each independently hydrogen, halide, a nitro group, a nitrile group, an imine, an amine, an ether group, a silyl ether group, a thioether group, a sulfoxide group, a sulfinate group, an acetylide group, an optionally substituted alkyl, an optionally substituted alkenyl, an optionally substituted alkynyl, an optionally substituted haloalkyl, an optionally substituted aryl, an optionally substituted heteroaryl, an optionally substituted alicyclic, or an optionally substituted heteroalicyclic; R₃ is optionally substituted alkylene, optionally substituted alkenylene, optionally substituted alkynylene, optionally substituted heteroalkylene, optionally substituted heteroalkenylene, optionally substituted heteroalkynylene, optionally substituted arylene, optionally substituted heteroarylene, or optionally substituted cycloalkylene, wherein alkylene, alkenylene, alkynylene, heteroalkylene, heteroalkenylene, and heteroalkynylene may optionally be interrupted by aryl, heteroaryl, alicyclic, or heteroalicyclic; R₄ is H, optionally substituted aliphatic, optionally substituted heteroaliphatic, optionally substituted alicyclic, optionally substituted heteroalicyclic, optionally substituted aryl, optionally substituted heteroaryl, optionally substituted alkylheteroaryl, or optionally substituted alkylaryl; R₅ is H, optionally substituted aliphatic, optionally substituted heteroaliphatic, optionally substituted alicyclic, optionally substituted heteroalicyclic, optionally substituted aryl, optionally substituted heteroaryl, optionally substituted alkylheteroaryl, or optionally substituted alkylaryl; E₁ is C, E₂ is O, S, or NH; or E₁ is N, and E₂ is O; Z is absent, or selected from -E-, -EX(E)-, or -EX(E)E-; X is C or S; each E is independently selected from O, S, or NR^(Z), wherein R^(Z) is H, optionally substituted aliphatic, optionally substituted heteroaliphatic, optionally substituted alicyclic, optionally substituted heteroalicyclic, optionally substituted aryl, optionally substituted heteroaryl, optionally substituted alkylaryl, or optionally substituted alkylheteroaryl; R is hydrogen, optionally substituted aliphatic, optionally substituted heteroaliphatic, alicyclic, optionally substituted heteroalicyclic, optionally substituted aryl, optionally substituted heteroaryl, optionally substituted alkylaryl, optionally substituted alkylheteroaryl, silyl, or a polymer; and when Z is absent, R may additionally be selected from halide, phosphinate, azide, or nitro; each G is independently absent, or a neutral or anionic donor ligand which is a Lewis base; M is Zn(II), Cr(II), Co(II), Mn(II), Mg(II), Fe(II), Ti(II), Cr(III)-Z—R, Co(III)-Z—R, Mn(III)-Z—R, Fe(III)-Z—R, Ca(II), Ge(II), Al(III)-Z—R, Ti(III)-Z—R, V(III)-Z—R, Ge(IV)-(—Z—R)₂, or Ti(IV)-(—Z—R)₂.
 5. The method according to claim 1, wherein each E is O.
 6. The method according to claim 1, wherein M is Zn(II) or Mg(II).
 7. The method according to claim 1, wherein the catalyst is selected from:

[L¹Mg₂Cl₂(methylimidazole)], [L₁Mg₂Cl₂(dimethylaminopyridine)], [L₁Mg₂Br₂(dimethylaminopyridine)], [L¹Zn₂(F₃CCOO)₂], [L¹Zn₂(OOCC(CH₃)₃)₂], [L¹Zn₂(OC₆H₅)₂], [L¹Fe₂Cl₄], [L¹Co₂(OAc)₃], [L¹Zn₂(adamantyl carbonate)₂], [L₁Zn₂(pentafluorobenzoate)₂], [L¹Zn₂(diphenylphosphinate)₂], [L¹Zn₂(bis(4-methoxy)phenyl phosphinate)₂], [L¹Zn₂(hexanoate)₂], [L¹Zn₂(octanoate)₂], [L¹Zn₂(dodecanoate)₂], [L¹Mg₂(F₃CCOO)₂], [L¹Mg₂Br₂], [L¹Zn₂(C₆F₅)₂], [L¹Zn₂(C₆H₅)₂], or [L¹Zn₂(OiPr)₂]; wherein [B—H]+ represents any counterion; and Nu is N-methylimidazole, pyridine, or dimethylaminopyridine.
 8. The method according to claim 1, wherein the catalyst system comprises a chain transfer agent.
 9. A polymer as produced by the method according to claim
 1. 10. The method according to claim 3, wherein the compound [Y] is an epoxide, an aziridine, an episulfide, an oxetane, a thietane, an azetidine, a saturated furan, a saturated thiophene, a pyrrolidine, or a saturated four-membered carbon ring where two adjacent carbon atoms are replaced by —Y—C(Y)—, wherein each Y is independently selected from O, S, or NR^(Y), and R^(Y) is H, optionally substituted aliphatic, optionally substituted heteroaliphatic, optionally substituted alicyclic, optionally substituted heteroalicyclic, optionally substituted aryl, optionally substituted heteroaryl, optionally substituted alkylaryl, or optionally substituted alkylheteroaryl.
 11. The method according to claim 3, wherein the compound [Y] is an epoxide.
 12. The method according to claim 4, wherein E₁ is C; and E₂ is O.
 13. The method according to claim 4, wherein R₁ is hydrogen, halide, an amine, an ether group, a thioether group, optionally substituted alkyl, optionally substituted alkenyl, optionally substituted alkynyl, optionally substituted haloalkyl, optionally substituted aryl, optionally substituted heteroaryl, optionally substituted alicyclic, or optionally substituted heteroalicyclic.
 14. The method according to claim 4, wherein R₂ is hydrogen, optionally substituted alkyl, optionally substituted aryl, or optionally substituted heteroaryl.
 15. The method according to claim 4, wherein R₄ is hydrogen, optionally substituted alkyl, optionally substituted aryl, or optionally substituted heteroaryl.
 16. The method according to claim 4, wherein R₅ is hydrogen, optionally substituted alkyl, optionally substituted aryl, or optionally substituted heteroaryl.
 17. The method according to claim 4, wherein M is selected from Zn(II), Mg(II), Co(II), Co(III)-Z—R, Cr(II), Cr(III)-Z—R, Mn(II), Mn(III)-Z—R, Al(III)-Z—R, Fe(II), or Fe(III)-Z—R.
 18. The method according to claim 1, wherein the epoxide has the following formula:

wherein each R^(e1), R^(e2), R^(e3), and R^(e4) is independently selected from hydrogen, halogen, hydroxyl, nitro, alkoxy, aryloxy, heteroaryloxy, amino, alkylamino, imine, nitrile, acetylide, carboxylate, optionally substituted aliphatic, optionally substituted heteroaliphatic, optionally substituted alicyclic, optionally substituted heteroalicyclic, optionally substituted aryl, optionally substituted heteroaryl, optionally substituted alkylaryl, optionally substituted alkylheteroaryl, or a polymeric species; or two or more of R^(e1), R^(e2), R^(e3), and R^(e4) can be taken together to form a saturated, partially saturated, or unsaturated 3 to 12 membered optionally substituted ring system, optionally containing one or more heteroatoms.
 19. The method according to claim 1, wherein the anhydride has the following formula:

wherein m″ is 1, 2, 3, 4, 5, or 6; each R^(a1), R^(a2), R^(a3), and R^(a4) is independently selected from hydrogen, halogen, hydroxyl, nitro, alkoxy, aryloxy, heteroaryloxy, amino, alkylamino, imine, nitrile, acetylide, carboxylate, optionally substituted aliphatic, optionally substituted heteroaliphatic, optionally substituted alicyclic, optionally substituted heteroalicyclic, optionally substituted aryl, optionally substituted heteroaryl, optionally substituted alkylaryl, optionally substituted alkylheteroaryl, or a polymeric species; or two or more of R^(e1), R^(e2), R^(e3), and R^(e4) can be taken together to form a saturated, partially saturated, or unsaturated 3 to 12 membered optionally substituted ring system, optionally containing one or more heteroatoms; or can be taken together to form a double bond; each Q is independently C, O, N, or S; and wherein R^(a3) and R^(a4) are either present, or absent, and

can either be

or —, according to the valency of Q.
 20. The method according to claim 1, wherein the lactone has the following formula:

wherein m is an integer from 1 to 20; and R^(L1) and R^(L2) are independently selected from hydrogen, halogen, hydroxyl, nitro, alkoxy, aryloxy, heteroaryloxy, amino, alkylamino, imine, nitrile, acetylide, carboxylate, optionally substituted aliphatic, optionally substituted heteroaliphatic, optionally substituted alicyclic, optionally substituted heteroalicyclic, optionally substituted aryl, optionally substituted heteroaryl, optionally substituted alkylaryl, or optionally substituted alkylheteroaryl; or wherein two or more of R^(L1) and R^(L2) can be taken together to form a saturated, partially saturated or unsaturated 3 to 12 membered optionally substituted ring system, optionally containing one or more heteroatoms. 